简介：对首钢长钢8号高炉铁口喷溅的原因与治理措施进行分析总结.通过采取采用炉体压浆技术、更换高质量炮泥、铁口压浆技术、铁口打孔放气、统一炉前操作、统一炉内操作等措施,喷溅逐步消去.

简介：La15Fe77B8hydrogenstoragealloyswerepreparedusingavacuuminduction-quenchingfurnace.TheresultsofX-raydiffraction(XRD)andscanningelectronmicroscopy(SEM)suggestedthatLa15–xSmxFe2Ni76Mn5B2(x=0,2,4,6)alloyshadmultiphasestructureincludingthemainLaNi5phase,La3Ni13B2phaseand(Fe,Ni)phase.WiththeincreasingsubstitutionofSmforLa,themainphasestructureofalloysdidnotchange,whiletheunitcellvolumesdecreased,thecyclestabilitywasimprovedandthemaximumdischargecapacitydecreased,butthelowtemperaturemaximumdischargecapacityofthesamesubstitutionalloywasgraduallyapproachingthemaximumdischargecapacityatroomtemperature,whichshowedthatLa15Fe77B8hydrogenstoragealloysofthepartialsubstitutionofSmforLahadbetterlow-temperaturedischargeability(LTD).Forthesamesubstitutionalloys,self-dischargecharacteristicsandcyclestabilityatlowtemperaturewerebetterthanthatatroomtemperature.Furthermore,thehigh-ratedischargeability(HRD)andtheexchangecurrentdensityI0firstincreasedandthendecreasedwiththeincreasingofSmcontent,whereasthehydrogendiffusioncoefficientDinalloybulkdecreasedgradually,whichindicatedthatappropriatesubstitutionofSmforLaimprovedtheelectrochemicalkineticspropertiesofthealloys.TheHRDwasmainlydominatedbythecharge-transferrateonthealloysurface.