简介：BasedonAPISTD1104-2005andCSAZ662-2007,fieldgirthweldingtestsandgirthweldabilityevaluationswereexecutedforthreetypesofwallthicknessX70UOEpipeline,inwhichthemostpopularmainlinegirthweldingmethod,single-wireautomaticgasmetalarcwelding(GMAW),wasused.Theweldingprocedurespecificationwasoptimizedtoachieveagoodqualityandcold-crack-freegirthweldjointwithoutpreheatingorpost-weldheattreatment.Inaddition,porosities,inclusions,andincompletefusiondefectswereavoided.Thetensilestrength,bending,Vickershardness,CharpyV-notchimpacttoughness,andcracktipopeningdisplacementfracturetoughnessofthegirthweldjointwereevaluated,andthejointexhibitedgoodmechanicalperformance.Thus,thefieldgirthweldabilityofBaosteel’sX70UOEpipelineisexcellentforautomaticGMAW.

简介：Separationisacommonlyobservedphenomenonduringdropweightteartestinginhigh-toughnesslinepipesteels.Severeseparationisharmfulbecauseitmaycausefracturingorburstingofpipes.Inthisstudy,aquantitativemeasurementofseparationwasproposed,andusingthisnewmethod,arelationshipbetweentheseparationandmicrostructurewasdeterminedanddiscussed.Themicrostructuresobservedusingopticalandscanningelectronmicroscopyrevealedthattheseparationwasrelatedtothemixedferriticandbainiticmicrostructures,orrather,itwasrelatedtothecarbonenrichmentinbainite.

简介：采用焊接热模拟技术,对其显微组织进行分析和冲击性能试验,研究了焊接线能量对X70管线钢焊接热影响区组织和力学性能的影响规律。结果表明,不同线能量下X70管线钢CGHAZ的组织主要是板条贝氏体（LB）、粒状贝氏体（GB）和准多边形铁素体（QF）。当热输入为20kJ/cm时,焊接热影响区组织以板条贝氏体为主,具有较好的冲击韧性。随着焊接线能量的增大,组织逐渐粗化,其韧性明显降低。