简介:Throughmeasuringthecoefficientoflinearexpansion,thestructureandpropertiesoftheLi2O-Al2O3-SiO2lowexpansionglassceramicscontainingB2O3arestudiedbyJRandXRD.ItisshoutnthattheIRmethodisefficientinthestudyoftheglass-ceramicsstructure.Thereisa"Boronabnormality"inthesystemwhichhasanimportantinfluenceonthepropertiesoftheglass-ceramics.
简介:TheelectronicstructuresofCuS2,CuSe2andCuTe2withpyritestructures,withintheframeworkthedensity-functionaltheoryhavebeeninvestigated.ThecalculatedresultsexplainedtherecentexperimentalresultswhichshowthatthereisnoclearindicationofstrongelectroncorrelationsintheelectronicpropertiesofCupyrites,duetothedominantchalcogenpcharacterratherthandcharacteristicofCuattheFermilevel.
简介:TheantibacterialeffectofcarryingsilverB2O3-SiO2-Na2Oglassmaterialwasstudiedbymeansofantibacterialring,nephelometery,MICvalue,thinfilmattachmentandmicrocalorimetry,respectively.TheexperimentalresultsoffivekindsofantibacterialtestmethodsarealmostidenticalandcanverifythatcarryingsilverB2O3-SiO2-Na2Oglassmaterialexertsanexcellentantibacterialperformance.Antibacterialringandnephelometeryaresimple,quick,buttheprecisionisrestrictive.MICvalue,thinfilmattachmentmethodandmicrocalorimetrycanquantitativelycomparetheantibacterialeffectsoftheantibacterialglassmaterial.Comparedwiththetraditionalmicrobetestmethods,themicrocalorimetrycananalyzetheinhibitingeffectofthecell'sgrowthandmetabolismontheantibacterialglassmaterialbymonitoringthethermaleffectcontinuouslyandautomatically.
简介:Newvisibletransparent,UVabsorption,andhighinfraredreflectionpropertieshavebeenrealizedbydepositingmultilayerSiO2/ZnO:Al/CeO2-TiO2/SiO2filmsontoglasssubstratesatlowtemperaturebyradiofrequencymagnetronsputtering.OptimumthicknessofSiO2,ZnO:Al(ZAO)andCeO2-TiO2(CTO)filmsweredesignedwiththeaidofthinfilmdesignsoftware.Thedegreeofantireflectioncanbecontrolledbyadjustingthethicknessandrefractiveindex.TheouterSiO2filmcandiminishtheinterferencecoloringandincreasethetransparency;theinnerSiO2filmimprovestheadhesionofthecoatingontheglasssubstrateandpreventsCa2+,Na+intheglasssubstratefromenteringtheZAOfilm.Theaveragetransmittanceinthevisiblelightrangeincreasesbynearly18%-20%,ascomparedtodoublelayerZAO/CTOfilms.Andthefilmsdisplayhighinfraredreflectionrateofabove75%inthewavelengthrangeof10-25μmandgoodUVabsorption(〉98%)properties.Thesesystemsareeasytoproduceonalargescaleatlowcostandexhibithighmechanicalandchemicaldurability.ThetriplefunctionalfilmswithhighUVabsorption,antireflectiveandhighinfraredreflectionratewilladapttoapplicationinflatpaneldisplayandarchitecturalcoatingglass,automotiveglass,withdiminishinglightpollutionaswellasdecreasingeyefatigueandincreasingcomfort.