简介:Nb-24Ti-18Si-2Al-2Hf-4CrandNb-24Ti-18Si-2Al-2Hf-8Cralloyswerepreparedbyarcmeltinginawater-cooledcrucibleunderargonatmosphere.Microstructuralcharacteristicsandoxidationresistanceofthealloysat1250℃wereinvestigated.Theresultsshowthat,whentheCrcontentis4at%,themicrostructuresconsistof(Nb,Ti)_(ss)andNb_5Si_3;asCrcontentincreasesto8at%,C14LavesphaseCr_2Nbisformed.Theisothermaloxidationtestsshowthattheoxidationkineticsofthetwoalloysfollowsimilarfeatures.Theweightgainsofthetwoalloysafteroxidationat1250℃for100hare235.61and198.50mg·cm~(-2),respectively.Duringoxidation,SiO_2,TiO_2,Nb_2O_5andCrNbO_4areformedatfirst.Then,Ti_2Nb_(10)O_(29)isformedafteroxidationfor20minandbeginstochangeintoTiNb_2O_7astheoxidationproceeds.SiO_2isformedassolidstateatfirstbutlaterevolvesintoglassystatetoimprovethecohesionofthescale.Afteroxidationfor100h,oxidationproductsconsistofSiO_2,TiNb_2O_7,Nb_2O_5andCrNbO_4.
简介:摘要对于高温、高压、临氢装置的TP321(国内为06Cr18Ni11Ti)奥氏体厚壁不锈钢钢管,由于其运行环境的特殊性,管道焊缝很容易产生晶间腐蚀,为了提高焊缝的抗高温腐蚀性能,焊后应进行稳定化热处理的工艺。本文对厚壁不锈钢管道焊缝稳定化热处理问题进行探讨,通过工艺评定和工程实践,成功解决了焊缝腐蚀问题。
简介:摘要目的观察黄金微针对13-18岁腋臭患者治疗的有效性和安全性。方法采用黄金微针对21例13-18岁腋臭患者进行1-2次治疗,对其疗效进行观察及分析。结果术后随访3-14个月,治愈9例,有效7例,无效5例。术后3例出现腋窝皮肤局灶性坏死,5例出现点状皮肤溃疡,经换药后痊愈;4例出现单侧腋窝及手臂皮肤麻木,经口服甲钴胺片,症状逐渐恢复。无效者3个月后接受第二次治疗。结论黄金微针治疗13-18岁腋臭患者具有安全,有效,恢复期短,不留疤痕,可以反复治疗等优点。