简介：本文研究了添加剂La2O3对FeNi粉末触媒合成金刚石的影响。实验结果表明，La2O3对金刚石的成核具有明显的抑制作用；借助于光学显微镜，我们发现Fe—La2PO3-C体系合成出的晶体晶形完整，但透明度变的很差，且表面变得很粗糙。

简介：2013年10月16日上午，深圳光韵达光电科技股份有限公司与比利时Materialise公司在上海就合作开展三维打印赛车项目签署协议，协议约定，整合双方优势资源，借助三维打印技术，用一年时间完成一辆可驾驶的电动或太阳能赛车的制作。

简介：PolycrystallinesamplesofLa12x(Sr12yAgy)xMnO3(y=0.0,0.2,0.4,0.6,1.0)werepreparedbythesolid-statereactionmethod.ThetemperaturestabilityofmagnetoresistanceandmagnetoresistanceenhancementinLa1-x(Sr1-yAgy)xMnO3systemwithbothunivalentandbivalentelementsdopedatAsiteandwithunchangedvalueofMn3+/Mn4+ratiowereexploredthroughthemeasurementsofX-raydiffractionpatterns,magnetiza-tion-temperature(M-T)curves,resistivity-temperature(q-T)curvesandmagnetoresistance-temperature(MR-T)curves.Theresultsareasfollows:therearetwopeaksintheq-TcurvesofthesampleswithAgdoping,oneiscausedbyresistancechangeduringtheparamagnetism-ferromagnetismtransition,andtheotherisfromboundary-dependentscatteringofconductionelectronsontheboundariesofgrains.ThepeakvalueofMRincreaseswithincreasingAgdopingcontent,anditincreasesfrom8.2%fory=0.2to29.6%fory=1.0underthemagneticfieldofB=0.8T;MRremainsaconstantof12%inthetemperaturerangeof218-168Kforthesamplewithy=1.0,andthetemperaturestabilityofMRisinfavorofthepracticalapplicationofMR.

简介：作为材料的重要性质之一，硬度一直受到人们广泛的重视和研究。Cohen和Liu利用第一性原理计算从理论上预言了一种超硬性能的新材料β—C3N4，其体积弹性模量超过金刚石。CVO3组采用微波等离子体化学气相沉积法(MPCVD)，用高纯N2(99．999％)和CH4(99．9％)作反应气体，在单晶Si(100)和多晶Pt衬底上沉积碳氮薄膜，开展了对β-C3N4薄膜的制备与表征的探索性研究，取得了一定的进展。

简介：有不同Y_2O_3内容的基于钴的合金被扔用血浆的onQ235A碳钢转移了焊接机器的弧(PTA)。微观结构上的Y_2O_3的效果并且穿基于钴的合金的抵抗性质用一台光显微镜，一台扫描电子显微镜(SEM)，X光检查衍射(XRD)，和传播电子被调查显微镜学(TEM)。有face-centeredcubic晶体结构的一个基于钴的稳固的答案被介绍，这被发现在Y_2O_3免费的基于钴的合金涂层与六角形的晶体结构由第二等的阶段M_7C_3伴随了。几叠差错在基于钴的稳固的答案存在。Y_2O_3的增加在修改Y_2O_3的涂层导致Y_2O_3阶段的存在。尽管叠差错在修改Y_2O_3的涂层存在，它的密度增加。Y_2O_3的增加能精制微观结构并且当它的内容小于等于0.8wt.%时，能增加wear抵抗性质。然而，它的内容的另外的增加将在γ-Cograin边界导致undissolvedY_2O_3粒子的凝块，并且将导致粗糙的微观结构并且降低穿抵抗性质。

简介：本文研究了经不同锻造工艺锻制的Ti-30Zr-5AI-3V合金棒材的四类显微组织:魏氏组织、网篮组织、双态组织和等轴组织。通过相同的热处理工艺处理后,研究不同显微组织对应的室温和400℃温性能。研究结果表明:添加30%的zr元素不会影响两相钛合金的相组成,通过适当的工艺可以获得魏氏、网篮、双态和等轴四类两相钛合金典型的组织类别;Ti-30Zr-5Al-3V合金的室温强度约在1100MPa以上,但延伸率很低,只有1O%左右;Ti-30Zr-5Al-3V合金的400℃高温强度可达900MPa以上,延伸率在9%~16%,400℃高温拉伸时的屈服强度约为700MPa。

简介：近日，StratasysLtd．子公司StratasysAsiaPacific宣布，Stratasys3D打印技术已成为主流，并开始为中国办公室自动化提供解决方案，帮助更多的企业受益于高效的概念模型和设计检验过程。为更好地支持和服务于中国地区逐渐增长的商业需求，

简介：pH价值和Y2Y23-SiO2(Y-Si)泥浆>为Ti-6Al-4V投资扔的脸上衣的O3粉末和硅石大音阶的第五音被测量。Y-Si脸上衣系统做的壳的热行为被微分扫描热量计(DSC)调查，热gravimetric(TG)分析与集体spectrometry(MS)结合了，并且阶段转变被X光检查衍射(XRD)决定。热力量，剩余力量，线性扩大系数，和壳的穿的抵抗性能也被测试。微观结构和相互作用层的元素分发被分别地扫描电子显微镜(SEM)和精力散的分光计(版本)学习。microhardness测试者被申请microhardness。结果证明泥浆为至少60是稳定的?h。YZrO3的很小的数量低于1050被形成?普牯慭?楦汥?桴潥祲?畢?畯?敲?瑬?灡汰?畱污瑩瑡癩汥?潴愠眠摩牥挠慬獳漠?睴?楤敭獮潩慮?楤慬潴?牧癡瑩?桴潥楲獥?潆?慥档琠灹?景猠汯瑵潩獮眠?数晲牯?潨潬牧灡楨?敲潮浲污穩瑡潩?挠浯異吗？？

简介：采用磁控溅射法成功制备Al2O3/Au层状复合纳米涂层,所制备的涂层结构致密且由Al2O3层和Au层交替组成。采用高温循环氧化实验对复合涂层在不锈钢基体上的高温抗氧化性能进行分析评价。结果表明：Al2O3/Au层状复合纳米涂层极大地改善不锈钢基体的抗氧化和抗剥落性能。其抗氧化机理与涂层能够有效地抑制氧向合金基体的扩散并促进不锈钢基体中Cr元素的选择性氧化有关;抗剥落机理可归因于复合涂层中的Au层和纳米结构的Al2O3层能够有效地松弛高温热循环过程中产生的热应力,从而提高涂层的抗剥落性能。

简介：Terrafugia使用SolidWorks3DCAD软件构建Transition模型，精确地计算出符合飞机和公路车辆双重安全和性能标准的数据。作为一款两栖车，Transition的重量必须足够轻，以便飞离地面；同时又需要足够坚固，以满足国家撞击安全法规要求，这就意味着需要尽可能减少材料用量。Terrafugia的策略是利用SolidWorks模拟产品精确地计算出在不减弱性能的前提下，

简介：通过水热法成功合成Co3O4/CuO复合物,并探索十六烷基三甲基溴化铵(CTAB)和聚乙烯吡咯烷酮(PVP)对其形貌和性能的影响。用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和氮气吸附-脱附测试表征其微观结构和表面形貌。采用循环伏安、恒流充放电和交流阻抗测试等方法研究样品的电化学性能。结果表明,多孔Co3O4/CuO-CTAB纳米片具有最好的电化学性能,在电流密度1A/g下的比容量达398F/g,而在10A/g时其比容量仍能保持90%。此外,该复合物具有很好的循环稳定性,在2000次循环后容量几乎没有衰减。

简介：Twinninganddetwinningaretheimportantdeformationmodesinmagnesiumalloysduringcyclicloadingatroomtemperature.Toanalyzethesetwodeformationmechanism,cycliccompression–tensionexperimentswereperformedonMg–3Al–1Znrolledsheetalongtherollingdirection.Inthesetests,themicrostructureevolutionsofaseriesofgrainsduringdeformationweretracedbyusingquasiinsituelectronbackscatterdiffraction(EBSD).ImportantquantitiesliketheSchmidfactorsoftwinningsystem,thefractionoftwinningduringcompression,andthefractionoftwinningafterreverseloadingwerecalculatedonthebasisofmeasuredquantities.TheinfluenceofSchmidfactoroftwinningvariantsondetwinninguponreverseloadingwasanalyzed.DetwinningwouldprefertoproceedduringreverseloadingiftheSchmidfactoroftwinninginthetwinningareabeforereverseloadingissufficientlylarge.

简介：TheeffectofAl-3Ti-0.2C-5Sr(wt%)grainrefinerontherefiningperformanceandmodificationofA356alloywasinvestigatedusingopticalmicroscope(OM).ThemorphologyandcrystalstructureofternaryAl-Ti-SrphasesinAl-3Ti-0.2C-5Srrefinerwereanalyzedbyscanningelectronmicroscopy(SEM)andtransmissionelectronmicroscopy(TEM).TheresultsshowthattheternaryAl-TiSrphasesinAl-3Ti-0.2C-5SrrefinercanpromotethegrainrefiningefficiencyofA356alloy.TheternaryAl-Ti-Srphasesco-existintwomorphologies,i.e.,blocky-likephaseandsurround-likephase,besides,whichbothhavethesamechemicalcompositionofAl_(34)Ti_3Sr.ThecrystalstructureofAl_(34)Ti_3Srisface-centeredcubic,andthelatticeparameterisdeterminedtobeabout1.52nm.

简介：Li1.3Al0.3Ti1.7(PO4)3pelletssinteredwithdifferentmolefractionsofLiBO2werepreparedbysol-gelmethod.Thestructuralidentification,surfacemorphology,ionicconductivity,andactivationenergyofthepelletswerestudiedbyX-raydiffraction,scanningelectronmicroscopy,andelectrochemicalimpedancespectroscopy.TheresultsshowthatalltheLi1.3Al0.3Ti1.7(PO4)3pelletssinteredwithdifferentmolefractionsofLiBO2havesimilarX-raydiffractionpatterns.ThesinteredpelletbecomesdenserandtheboundaryandcorneroftheparticlesbecomeillegiblewiththeincreaseofLiBO2.AmongtheLi1.3Al0.3Ti1.7(PO3)4pelletssinteredwithdifferentmolefractionsofLiBO2,theonesinteredwith1mol%LiBO2showsthehighestionicconductivityof3.95×10-4S.cm-1andthelowestactivationenergyof0.2469eV.

简介：钛酸铝系复合材料中钛酸铝的体积分数不同，会导致Al2TiO5／Al2O3复合材料的抗铝液浸渗性能的不同。在Al2TiO5中分别按10％、20％、40％、60％、80％、90％（体积分数）引入Al2O3进行复合。通过对渗铝试样的外观形貌、微观结构分析，进而对其铝液浸渗性能进行了分析比较，发现富钛酸铝的钛酸铝／氧化铝复合材料（妒（AL2TiO5）〉40％）抗铝液浸渗性能好；而富氧化铝的钛酸铝／氧化铝复合材料（φ（Al2TiO5）〈20％）有金属铝液沿热震产生的裂纹渗入复合材料内部，容易导致复合材料断裂失效。该研究结果对可靠应用钛酸铝系复合材料作为铝液的容器具有实际工程应用价值。

简介：

简介：基于炉渣结构分子和离子共存理论,建立1273-1733K下的PbO-CaO-SiO2-FeO-Fe2O3渣系氧化铅活度热力学模型,计算PbO活度并绘制等活度曲线,考察炉渣碱度Q、氧化铁比率R和温度T对活度NPbO和活度系数γPbO的影响。结果表明,活度系数γPbO的模型计算值与文献测定值吻合程度高,说明该模型能较好地反映该渣系结构本质;NPbO呈拉乌尔正偏差,且随渣中PbO含量的升高而增大,但受温度的影响不明显;γPbO随Q的升高而增大;对于Q〉0.3的碱性渣,γPbO随R的升高而出现极大值。该研究结果可用于现代炼铅工艺的热力学研究和操作优化。

简介：在823K和973K的条件下,采用恒电流密度共电沉积法在LiCl-KCl-MgCl2-Gd2O3熔盐体系中制备Mg-Li-Gd合金,并运用XRD、SEM、EDS和OM对所制备合金进行微观组织分析。结果表明:在开始的30min内,主要是Mg和Gd的沉积,所得合金含96.53%Mg,3.20%Gd和0.27%Li(质量分数),然后Li迅速沉积。可以通过控制电解时间或改变Gd2O3的浓度调节Mg-Li-Gd合金的组成。XRD分析可知,在Mg-Li-Gd合金中存在Mg3Gd相和Mg2Gd相。从Gd元素的面扫描分析可知,Gd元素主要分布在Mg-Li-Gd合金的晶界处。Gd的添加增强了合金的抗腐蚀能力。

简介：中国人民银行定于2010年3月23日发行中国古典文学名著——《水浒传》彩色金银纪念币（第2组）一套。该套纪念币共5枚，其中金币2枚，银币3枚，均为中华人民共和国法定货币。该套纪念币发行规格为1／3盎司彩色圆形金质纪念币，最大发行量为35000枚；5盎司彩色长方形金质纪念币，最大发行量为900枚；1盎司彩色圆形银质纪念币（2枚），最大发行量各为70000枚；5盎司彩色长方形银质纪念币，最大发行量为12000枚。

简介：1Cr15Ni4Mo3N沉淀硬化不锈钢螺栓零件在制造工序磁粉检测时，发现螺栓表面有一条疑似裂纹状线性磁痕显示，后采用荧光渗透检测方法进行辅助检测，原磁痕显示处未见异常荧光显示。结合金相试验分析发现，螺栓原材料内呈带状分布的残余奥氏体，破坏了基体组织和材料磁性的连续性导致出现磁痕显示。研究为该材料在零件制造中磁粉检测的磁痕判定提供了依据。