简介：

简介：以川西微晶白云母为主要原料，铝粉为还原剂，采用铝热还原氮化法合成了α-Al2O3／β-SiAlON材料，并利用X射线衍射仪（XRD）研究了不同温度下的物相变化及配铝量对反应产物的影响。结果表明：在1350℃和1450℃,所有样品的主要产物均为α-Al2O3和β-SiAlON相，但铝粉用量为35％（质量分数，下同）的样品经1350℃铝热还原氮化后的产物中含β-SiAlON相较多；当铝粉用量和加热温度分别为45％和1550℃时，反应产物中不含α-Al2O3和β-SiAlON相，却出现了AlON、AlON和Si3Al7O3N9相。

简介：WithFe(NO3)39H2OandBi(NO3)35H2Oasrawmaterials,differentsillenite-typecompoundsandelementalbismuthwerepreparedbyafacileone-potsolvothermalmethodusingH2O,C2H5OH,(CH2OH)2andC3H8O3assolvents,respec-tively.Thestructure,morphology,elementalcompositionsandpropertiesofsampleswereexaminedbyXRD,SEM,TEM,ICP,XPS,N2adsorptionanddesorption,UV-visDRSandPL.ThephotocatalyticactivitiesofdifferentsampleswereevaluatedbythephotodegradationofRhBundervisible-lightirradiation(λ>400nm),andresultsshowthatBi36Fe2O57preparedusingC2H5OHasthesolventownstheoptimumperformance.Inordertoexplorethereactionmechanism,anadditionalexperimentwasdesignedtoinvestigatethemainactivespeciesduringthephotodegradationprocessviadissolvingdifferenttrappingagentsinthereactionsolutionbeforelightirradiation.TheresultsshowthatsuperoxideradicalanionsplayamajorroleinthissystemsincetheRhBdegradationwassignificantlysuppressedaftertheadditionofbenzoquinone.

简介：以两种Al2O3-Al2TiO5复合粉体为原料经SPS烧结制备出Al2O3-Al2TiO5复相陶瓷。采用纳米结构复合粉体烧结而成的复相陶瓷有着较优的力学性能，特别是具有较高的断裂韧性和硬度，与其较小的晶粒尺寸相对应。干滑动摩擦磨损试验在4N和6N法向载荷下进行，结果表明，采用微米结构复合粉体烧结而成的复相陶瓷磨损表面较光滑，体积磨损量较小。在磨损试验中，纳米结构复合粉体烧结而成的复相陶瓷的破坏方式为沿晶断裂，有明显的晶粒拔出现象；微米结构复合粉体烧结而成的复相陶瓷呈不连续的微观断裂并产生塑性变形；同时，两种材料在摩擦磨损过程中都发生接触面的氧化和物质转移。

简介：

简介：利用异烟酰肼和2-羟基-3-甲氧基苯甲醛（邻香草醛）合成了一种新的Schiff碱-2-羟基-3-甲氧基苯甲醛异烟酰腙（L），并制备其Cu（Ⅱ）、Cd（Ⅱ）、Zn（Ⅱ）的配合物。利用元素分析、摩尔电导、红外光谱、紫外光谱、差热分析等手段对该Schiff碱及其配合物进行了表征，得到了Schiff碱及其配合物的推测组成，并研究了配体和配合物的荧光光谱，结果表明锌和镉的配合物与配体相比具有较好的荧光特性。

简介：

简介：以一步水热法制备了具有分级结构的泡沫镍@C/氧化钴复合电极材料,研究了该材料的微观形貌结构以及其超级电容特性.结果表明,在1mol/LKOH溶液中,泡沫镍@C/Co3O4复合超级电容器电极材料电化学性能良好,面积比容量达1400mF/cm2.

简介：采用机械球磨技术制备了MgH2-10％Al2O3（质量分数）储氢复合体系,通过XRD、SEM、DSC-TG等检测手段考查了微量Al2O3陶瓷颗粒掺杂对MgH2体系组织结构及解氢性能的影响,并对其相关机理进行了分析.结果表明：机械球磨可有效细化MgH2颗粒;在微量Al2O3陶瓷颗粒与机械球磨的协同作用下,MgH2颗粒的细化效果更为显著;相对于纯MgH2球磨体系而言,微量Al2O3的掺杂有效降低了MgH2体系的解氢温度（降低近50℃）,且其解氢速率也有所提高;MgH2-Al2O3储氢复合体系解氢性能的改善主要源于Al2O3陶瓷颗粒对MgH2体系的组织细化效应.

简介：研究了去离子水作为球磨介质对Mn掺杂（Na0．5Bi0．5）0．88Ca0．12TiO3（BNCT）陶瓷介电性能的影响。相对于酒精，水磨样品的介电常数较小。介电常数温度曲线以及电容变化率温度曲线都比较平坦，在-55～250℃范围内，△C／G25℃≤±15％。介电损耗在100C以上时明显增大。比较和分析了XRD图谱和SEM图片，并借助于EDS探讨了微观机理。

简介：钛酸锶钡（BST）陶瓷是一种性能优异的电容器材料、热敏材料和铁电压电材料，具有非常广阔的应用领域。采用溶胶-凝胶法合成了Ba0．6Sr0．4TiO3纳米粉体，通过X射线衍射仪（XRD）、扫描电子显微镜（SEM）、激光粒度分析仪对粉体的物相组成、颗粒大小和形态进行了分析，利用红外光谱仪（FT～IR）研究了表面活性剂在合成纳米Ba0．6Sr0．4TiO3过程中的作用，并重点考察了表面活性剂对Ba0．6Sr0．4TiO3粉体性能的影响。研究结果表明，通过添加适量的表面活性剂能有效改善纳米钛酸锶钡粉体的表面性能，使纳米钛酸锶钡具有较好的分散性，可充分发挥材料的纳米效应。

简介：制备了SO3H／SiO2自组装单层纳米膜材料，并用其在水中的质子化效应进行表征。用SO3H／SiO2作为吸附剂处理低浓度五氯酚（PCP）有机废水取得了良好的吸附效果。通过调节／不调节pH值对比吸附实验，推测PCP在SO3H／SiO2自组装单层表面的吸附机理为氢键吸附。

简介：Anitrate-citratecombustionroutetosynthesizeLa0.9Sr0.1Ga0.8Mg0.2O3-δpowderforsolidoxidefuelcellapplicationwaspresented.Thisrouteisbasedonthegellingofnitratesolutionsbytheadditionofcitricacidandammoniumhydroxide,followedbyanintensecombustionprocessduetoanexothermicredoxreactionbetweennitrateandcitrateions.TheoptimumtechnicalparametersarethatthepHvalueis5,andthemolarratioofcitricacidtothetotalmetallicionis1.5:1.X-raydiffractioncharacterizationofcalcinedgelshowsthatpurephasewassynthesizedaftercalcinationat1400℃for10h,andtheTEMresultshowsthecalcinedpowderwithaverageparticlesizeisabout150nm.Thegrainresistancecontributestothetotalresistanceofsinteredpelletbelow500℃.Theconductivityofthesinteredpellentat800℃was0.07S-1.cm-1higherthantheconductivityofYSZ(0.05S-1.cm-1at800℃)

简介：包含Pechini方法和火花血浆sintering(SPS)方法的一条典型途径为高密度Li5+xSrxLa3xBi2O12的准备被介绍(x=0，1)陶艺。阶段形成，微观结构，谷物尺寸和标本的电的性质用XRD，SEM和交流电阻抗光谱学(酸)被检验。有纯像石榴石的阶段，97%的相对密度和大约5m的平均谷物尺寸的稠密的Li5La3Bi2O12和Li6SrLa2Bi2O12陶艺用这条途径被制作。在陶艺由SPS方法准备了的Li5La3Bi2O12和Li6SrLa2Bi2O12的298K的全部的传导性是5.1吗？？

简介：

简介：采用柠檬酸溶胶-凝胶法制备了稀土Gd3＋掺杂的LaPU新型热障涂层用陶瓷粉体LaPO4（X=0．0，0．1，0．2，0．3；LGPO）。通过X-ray衍射、扫描电子显微镜、TpDSC、高温热膨胀仪和激光热导仪对样品的相组成、微观形貌、热行为、热膨胀系数和热导率进行表征。结果表明：稀土Gd3＋掺杂的LGPO保持了独居石相结构；添加稀土Gd3＋不仅可以降低材料的导热系数，还有利于其热膨胀系数的提高；随着稀土Gd3＋掺杂量的增加，晶体中点缺陷浓度不断升高，声子平均自由程不断减小，使得稀土Gd3＋掺杂的LGPO的热导率在x=0．3时达到最低值（λ=1．22w／（m·K），T=1273K），该值明显低于同温度下8YSZ的热导率。Gd3＋掺杂的LaPO4体系是下一代新型热障涂层用陶瓷热门的候选材料之一。

简介：这研究调查了退火的效果一张同样滚动的Mg-9.26wt.%Li-3.03wt.%Al-1.10wt.%Zn(LAZ931)合金表的机械性质上的温度。双阶段(+)在厚度的3公里的LAZ931合金板被卷(67%减小)然后在100点在温度退火了????$

简介：Si_3N_4-Si_2N_2Ocomposites被液相sintering(LPS)与非结晶的缩放nano的氮化矽粉末制作。Si_2N_2O阶段被in-situreaction2Si_3N_4(s)+1.5O_2(g)=3Si_2N_2O+N_2(g)产生直到在体积的60percent的Si_2N_2O阶段的内容在1650t的sintering温度被获得并且当sintering温度增加了或减少时，减少了，显示反应是可逆的。集体损失，相对密度和平均谷物尺寸与增加sintering温度增加了。当sintering温度在1700degC下面时，Theaverage谷物尺寸是不到500nm。Thesintering过程包含复杂结晶化和阶段转变：非结晶的氮化矽->equiaxialalpha-Si_3N_4->equiaxial->Si_3N_4->杆--相似Si_2N_2O->像针的beta-Si_3N_4。小回合--塑造的beta-Si_3N_4粒子在Si_2N_2O谷物被骗诱，界定差错的高密度位于在1650degC的sintering温度的Si_2N_2O谷物的中间。坚韧在1600degCto7.2MPa从3.5Mpa中心点m~(1/2)增加了在1800degC的中心点m~(1/2)。坚硬在1600degC象21.5GPa(Vickers)一样高。

简介：采用自制的BA-MMA-AA三元共聚物和四异丙氧基钛（TPT）对纳米Si3N4进行表面包覆处理,利用红外光谱分析、TEM、粒径分布、接触角等手段进行表征,结果表明：在纳米Si3N4粉体的表面包覆了有机物,并与其发生了化学作用,有效地阻止了纳米Si3N4粉体的团聚;处理过的Si3N4粉体粒径明显减小,在有机溶剂中的分散稳定性显著增加,表面自由能明显降低,改善了纳米Si3N4粉体在聚合物基体中的分散。

简介：利用DTA、XRD研究了Y2O3的添加对CaO-MgO-SiO2系陶瓷纤维析晶行为的影响。根据Ozawa和Kissinger法对系统中析晶活化能的计算结果表明，少量Y2O3的添加并没有改变材料中析出的晶相种类，但是可以提高玻璃化转变温度和析晶温度，增大晶相的析晶活化能，从而能够在一定程度上抑制材料中晶相的析出。