简介:Inthisstudy,weinvestigatedtheeffectsof6-benzylaminopurine(6-BA)–calciumchloride(CaCl2)–salicylicacid(SA)treatmentontheyellowingandreactiveoxygenmetabolismofharvestedbroccoliheads.Wedippedfreshbroccoliheadsinacompoundsolution(0.6mmol/L6-BA+40mmol/LCaCl2+3mmol/LSA)for5minandthenstoredthemat23°Cfor4days.Theresultsshowedthatthe6-BA–CaCl2–SApostharvesttreatmenteffectivelyretardedtheincreaseincolorvalues(e.g.,variationsfromblacktowhite,fromgreentored,andfrombluetoyellow)andthedeclineinchlorophyllcontentofthebroccoliheads.Comparedwiththecontrolbroccoli,therateofsuperoxideanionradical(O2·?)productionandthehydrogenperoxide(H2O2)contentwereloweredbythetreatment.Wealsofoundsignificantdifferencesintheactivitiesofsuperoxidedismutase(SOD),catalase(CAT)andperoxidase(POD)inthetreatedbroccoli.Basedontheseresults,weconsider6-BA–CaCl2–SAtoinhibittheaccumulationofreactiveoxygen,delaythedegradationofchlorophyll,andprolongtheshelflifeofbroccoliheadsat23°C.
简介:采用原位聚合法制备一组CoFe204含量不同的CoFe204/PA6磁性纳米复合材料并对其性能进行表征。TEM结果显示CoFe204在复合材料中分散达到纳米级,但是团聚现象比较严重;XRD结果表明随着CoFe204含量的增加复合材料中出现了CoFe204特征峰,另外CoFe204的加入对基体材料PA6晶型影响不大;VSM结果显示复合材料的饱和磁化强度和矫顽力随着CoFe204含量的增加而增加,样品5的比饱和磁化强度达到3.5eum/g左右;DSC结果表明CoFe204加入会阻碍PA67晶型的形成;CoFe204的含量越高复合材料的热稳定性越低。
简介:以PMMA作为基质材料,以Coumarin6作为荧光物质,采用掺杂方式制备出平面荧光太阳能聚光器。制备得到的Coumarin6平面荧光太阳能聚光器的几何尺寸分别为50mm×50mm×5mm与100mm×100mm×5mm,将太阳能电池粘贴于聚光器的输出端,通过测试聚光器对太阳能电池输出功率的影响测定Coumarin6平面荧光太阳能聚光器的聚光特性。而为了研究掺杂浓度对聚光器聚光特性的影响,制备了7种不同浓度的Coumarin6平面荧光太阳能聚光器,并分别测试了其聚光特性,得出最优化的掺杂浓度。
简介:本文采用水热法在不同的条件下(不同温度、不同pH值、不同浓度的表面活性剂)制备了可见光催化剂Bi2WO6,同时也掺杂了Fe制备了Bi2WO6,并改变了原材料的配比,制备了Bi2O3-Bi2WO6。实验结果表明:Bi2WO6的禁带宽度在2.83eV,有良好的可见光催化性能。Bi2O3-Bi2WO6拓宽了禁带宽度,使得禁带宽度为3.05eV。催化剂的光催化活性和催化剂的晶型、颗粒的半径大小、比表面积的大小都密切相关。然而催化剂的形貌、粒径、比表面积又与制备条件密切相关,只有在特定形貌下,粒径小并且均匀的情况下的催化剂的催化活性才好。在酸性条件下由于抑制了硝酸铋的水解,从而制备的催化剂的催化活性优于在碱性条件下制备的催化剂。催化剂在降解罗丹明B的实验中,催化时的去乙基作用使得罗丹明B溶液的主峰发生蓝移,主峰由553nm移动到了495nm。催化剂的去乙基作用于只有在可见光的照射下才会发生,并且去乙基作用使得光催化降解反应的初速度加快。催化剂的吸附性能影响去乙基反应,吸附性能差的催化剂发生去乙基反应的速度也低。催化剂在降解染料时对染料有选择性,本实验所制备的催化剂对罗丹明B的降解效果高于对甲基橙的降解效果。