简介:Thesegregationanddiffusionofboronduringheattreatmentswerestudied.Theinfluenceofboroncontents,agingtimeandappliedstressonFeMo2B2formationwasalsostudied.Finally,theeffectsofboroncontentsandFeMo2B2formationonthehightemperaturestrengthwerestudied.Boronatomsweresegregatedtoprioraustenitegrainboundaryduringnormalizingtreatment.Andtheseboronatomswereslowlydiffusedintothegraininteriorduringtemperingandagingat700℃.TheFeMo2B2phasewasonlyformedafter1,000hagingat700℃inalloycontaining196ppmboron.TheformationofFeMo2B2phaseisacceleratedbytheappliedstress.ItwasexpectedthattheformationofFeMo2B2iscloselyrelatedtotheredistributionofboronatoms.Thetensilestrengthsat700℃areincreasedwiththeincreaseofboroncontents.However,theformationofFeMo2B2phaseresultsinlowertensilestrength.
简介:TooptimizethemagneticpropertiesofnanocompositeNd9Fe85B6magnets,theas-quenchedribbonswithdifferentmicrostructureswerepreparedatsixwheelvelocitiesfrom10to30ms-1throughrapidquenching,followedbyaseriesofannealingtreatmentsat550–800°Cfor5–10min.Itisfoundthatboththelargeinitialgrainsatlowcoolingrateandhighcontentofamorphousphaseathighcoolingratecausea-Fegrainscoarsening,whichleadstoadeclineinthestrengthofexchangecouplinginteractionandthedeteriorationofmagneticproperties.Inordertooptimizethemagneticproperties,theas-quenchedribbonsshouldbechosenwithrelativelysmallinitialgrainsaswellasasmallamountofamorphousphase.FornanocompositeNd9Fe85B6materials,theoptimizedmagneticpropertiesofHcj=446kAm-1,Br=0.86T,(BH)max=80kJm-3areobtainedforribbonspreparedat18ms-1afterannealingat620°Cfor5min.
简介:ThemicrostructureandtensilepropertiesofSn-9Znsolderunderdifferentcoolingandagingconditionwerestudied.Duringsolidification,thedistributionofZn-richphasesandgrainsizeinthemicrostructureofSn-9Znsolderweredecidedbythecoolingrate.TheZn-richphaseinSn-9Znsolderunderfurnacecooling,aircoolingandwatercoolingmediawasseparatelyexistedascoarsendendriticandneedlelikeshape,fineneedlelikeshapeandveryfinerod-likeshape,respectively.Afteraging,thecoarsendendriticwasbrokenandthecoarsenneedlelikeZn-richphasewaspartlychangedintofinedistributionofZn-richphaseforSn-9Znsolderwithfurnacecooling,andtherod-likeZnphaseintheSn-9ZnsolderunderwatercoolingwaschangedtoconglomeratedZnwithneedleshape.DuringtensiletestingonSn-9Znsolder,tensilestrengthandductilityreachedthebestwithwatercooling,butdecreasedwithagingeffect.Meanwhile,theductilityofsolderwithaircoolingandthestrengthofsolderwithfurnacecoolingincreasedwithaging.Thefracturemodewasductileandwasindependentofcoolingmediaandagingeffect.Thesizeanddepthofdimplesdecreasedfromwater,furnacetoaircooling.Afteraging,numberandsizeofdimplesincreasedonthesolderwithfurnacecoolingandaircooling.ThechangeonthesizeofdimplesfortheSn-9Znsolderunderdifferentcoolingconditionandwithagingeffectwasaccordancetothetensileproperties.