简介:ThemicrostructureandopticalpropertiesofaburiedlayerformedbyO+(200keV,1.8×1018/cm2)andN+(180keV,4×1017/cm2)co-implantationandannealedat1200℃for2hhavebeeninvestigatedbyAugerelectron,IRabsorptionandreflectionspectroscopicmeasurements.TheresultsshowthattheburiedlayerconsistsofsilicondioxideandSiOx(x<2)andthenitrogensegregatestothewingsoftheburiedlayerwhereitformsanoxynitride.BydetailtheoreticalanalysisandcomputersimulationoftheIRreflectioninterferencespectrum,therefractiveindexprofilesoftheburiedlayerwereobtained.
简介:Organicmultiplequantumwells(OMQWs)consistingofalternatinglayersoforganicmaterialshavebeenfabricatedfromtris(8-hdroxyquinoline)aluminum(Alq)and2-(4-biphenylyl)-5-(4-tertbutylphenyl)-1,3,3-oxadiazole(PBD)byamultisource-typehigh-vacuumorganicmoleculardeposition.Fromthesmall-angleX-raydiffractionpatternsofAlq/PBDOMQWs,aperiodicallylayeredstructureisconfirmedthroughtheentirestack.TheAlqlayerthicknessintheOMQWswasvariedfrom1nmto4nm.Fromtheopticalaborption,photoluminescenceandelectroluminescencemeasurements,itisfoundthattheexcitonenergyshiftstohigherenergywithdecreasingAlqlayerthickness,ThechangesoftheexcitonenergycouldbeinterpretedastheconfinementeffectsofexcitonintheAlqthinlayers.Narrowingoftheemissionspectrumhasalsobeenobservedfortheelectroluminescentdevices(ELDs)withtheOMQWsstructureatroomtemperature.
简介:Aneworganicsemiconductortartaricaciddopedsaltofemeraldinepolyaniline(PANI-C4H6O6)hasbeenobtainedbythemethodofoxidativepolymerizationofmonomericanilinewithammoniumpersulfateinacidicsolution.ThestructurewascharacterizedbyFourierTransformInfraredtechnique(FTIR)andX-raydiffraction(XRD).Thetemperaturedependencedcconductivityδdc(T)showsasemiconductorbehaviorandfollowsthequasionedimensionalvariablerangehopping(Q1D-VRH)model.Dataonδdc(T)arealsodiscussed.
简介:Aprocesssuitableforproductiononalargescaleofcoldlightmirrorforfilmprojectorisintroduced.DepositionparametersrequiredforproducingTiO2/SiO2opticalmultialyersystemsbyelectronbeamevaporationofTiO2andSiO2startingmaterialsareinvestigated.Manufactureandtechniquesofcoldmirrorandtheadhesion,stability,wearandcorrosionresistanceofcoldmirrorbythisprocessarediscussed.Theresultshowsthatcoldmirrorproducedhasgoodopticalpropertiesandbetteradhesion.