简介：ExtractingB2O3fromcalcinedboronmud(CBM)wasstudied.TheeffectoffactorssuchasreactiontemperatureandNaOH-to-CBMmassratioonB2O3extractionefficiencywasinvestigated.TheresultsshowthatincreasingreactiontemperatureandNaOH-to-CBMmassratioincreasesB2O3extractionefficiency.TherearetwostagesfortheB2O3extractingprocess:0–20ministhefirststage,whichisrapid;20–50ministhesecondstage,whichisslowerthanthefirststage.Theoverallextractingprocessfollowstheshrinkingcoremodel,andthefirstandsecondstagesaredeterminedtoobeythesurfacechemicalreactionmodelandthediffusionthroughtheproductslayermodel,respectively.Theactivationenergiesofthefirstandsecondstagesarecalculatedtobe41.74and15.43kJ·mol-1,respectively.TheB2O3extractingkineticsequationsofthefirstandsecondstagesarealsoobtained.

简介：CaTiO3的形成行为在钛铁矿的electro-deoxidization期间专注准备FeTi合金被实验和模拟调查。结果显示中间的产品的形成和分解，CaTiO3,在钛铁矿的electro-deoxidization期间是不可避免的步专注。CaTiO3能在电气化学的过程期间通过熔融的盐和电气化学反应的hydrolyzation被产生。为CaTiO3的产生的主要原因在阴极是在从熔融的盐和TiO2的Ca2+之间的电气化学反应。与electro-deoxidization继续，CaTiO3是进一步的electrolyzed形成钛低值氧化物。当在由在sintering期间增加CaCO3的阴极的CaTiO3形式处理时，当前的效率能被改进。

简介：ＥｐｉｔａｘｉａｌＧｒｏｗｔｈｏｆＹＢＣＯＴｈｉｎＦｉｌｍｓｏｎＬａＡｌＯ＿３ＳｕｂｓｔｒａｔｅｗｉｔｈＣｅＯ＿２ＢｕｆｆｅｒＬａｙｅｒＭａＰｉｎｇ，ＹａｎｇＪｉａｎ，ＧｕＨｏｎｇｗｅｉ，ＣｈｅｎＬａｎｆｅｎｇａｎｄＣｈａｎｇＳｈｉａｎ（马平）（杨坚...

简介：据香港统计局4月25日公布的数据显示，由于买家利用金价3月下跌的机会买入黄金，中国大陆当月从香港进口的黄金规模达到2015年12月来的最高水平。

简介：第十八届中国国际投资贸易洽谈会8日在此间举行。联合国贸易发展会议在会上发布的《2014年贸易与发展报告》称，2014年全球经济预期增长2．5％至3％。报告称整个发展中经济体很可能会重复过去几年的业绩，增长率在4．5％到5％之间。在这一组国家中，亚洲和撒哈拉以南国家的增长率将超过5．5％。

简介：高质量的取向附生的YBa2Cu3O7-(YBCO)超导的电影被制作在上(OOl)用直流的劈啪作响方法的LaAlO3底层。不平常地高的电影厚度的成就(多达2.0嗯)没有microcracking，部分地被归因于毛孔的存在在这些电影与充满钇的作文相关。微观结构上的电影厚度的影响被X光检查衍射调查常规扫描(-2,-scan,杆数字)和印射的高分辨率的相互的空间。电影是没有直到2m的厚度的a-axis-oriented谷物面向的c轴。表面形态学和批评当前的密度(Jc)强烈取决于电影厚度。而且，为这些厚度依赖的原因详细被阐明。

简介：ＥｌｅｃｔｒｏｃｒｙｓｔａｌｌｉｚａｔｉｏｎＭｅｃｈａｎｉｓｍｏｆＴｕｎｇｓｔｅｎｉｎＭｏｌｔｅｎＫＦ－Ｂ＿２Ｏ＿３－Ｋ＿２ＷＯ＿４ＷｅｎＺｈｅｎｈｕａｎａｎｄＬｉＧｕｏｘｕｎ文振环，李国勋（ＧｅｎｅｒａｌＲｅｓｅａｒｃｈＩｎｓｔｉｉｕｔｅｆｏｒＮｏ...

简介：polyacrylonitrile(平底锅)上的electrodepositingFe-Cr2O3合成涂层的过程基于碳纤维，它的催化graphitization被学习。有或没有electrodepositedFe-Cr2O3合成涂层的碳纤维是在不同温度对待的热，结构的变化被XRD，拉曼光谱学和SEM描绘。结果显示那Fe-Cr2O3合成涂层在低温度在碳纤维的graphitization上展出重要催化效果。当Fe-Cr2O3-coated碳纤维是时，热对待在1300?慢敳?慣'R湯映扩牥映汥?獡琠敨瀠敲畣獲牯映汯潬敷?祢椠灭敲湧瑡潩?楷桴爠獥湩?潭摬湩?湡?敨瑡琭敲瑡敭瑮楴?楴吗？？

简介：Thecorrosionfatiguebehaviorofepoxy-coatedMg–3Al–1Znalloywasinvestigatedinairand3.5wt%NaClsolution.Epoxycoatingasanewmethodwasusedtoimprovethecorrosionfatiguepropertyofthematerial.Resultsshowthatthefatiguelimit(FL)ofthecoatedspecimensishigherthanthatoftheuncoatedspecimensin3.5wt%NaClsolutionbecauseofthestrengtheningandblockingfunctionsoftheepoxycoating.TheFLofthecoatedspecimensin3.5wt%NaClsolutionisashighasthatinair.Itimpliesthatthecoatedspecimensarenotassensitivetotheenvironmentasthemagnesiumalloy.Thelowtensilestrengthandtheshortelongationofthepureepoxycoatingleadtothatthefatiguecrackofthecoatedspecimenisalwaysinitiatedfromtheepoxy-coatingfilmPoresandpinholesacceleratethefatiguecrackinitiationprocess.PinholesarecausedbythecorrosionreactionsbetweentheepoxycoatingandtheNaClsolution.

简介：Solventextractionofpalladium(Ⅱ)fromhydrochloricacidsolutionwith2-n-octyl-4-isothiazolin-3-one(OIT)/cyclohexanewasstudied.Effectsofdifferentparametersonextractionefficiencywereevaluated.99.96%and98.26%palladium(Ⅱ)couldbeeffectivelyextractedwith0.018mol·L-1OIT/cyclohexaneof0.1and4.0mol·L-1HClmedium,respectively.Nonpolarsolventandlowaciditycouldimprovetheextractingefficiency,andsuccessfullystrippalladium(Ⅱ)fromtheloadedorganicphasewasachievedwith0.5mol·L-1(NH2)2CSsolution.ItwasproposedthattheextractionofPdcomplexesfromHClmediumproceededthroughtheionassociationmechanismbyslopemethod,NMRandFT-IRspectra.

简介：AnewtypeofcomplexsolidsuperacidcatalystWO3-ZrO2-SO42-withanacidstrengthH0≤-16.04waspreparedbykneadingZr（OH）4oramorphousZrO2withtungsticacid（H2WO4）（W/Zr=0.15）,followedbyexposingthiscomplexhydroxidesto0.5tool/LH2SO4,calcininginairat700～800℃for3h.ThiscatalystpossessesbothstrongBronstedacidityandstrongLewisacidityexperimentallyshowedbyIRobservationofpyridineabsorbedonit.XPSandAEStechniqueswereemployedtoexaminethevalencestatesoftungsten,zirconium,sulfurandtheirinteractions.Thestructureofsulfurspecieswasstudiedbyinfraredspectroscopyandastructuremodelofactivesitewasproposedupontheseresults.

简介：采用TMPAC-AlCl3离子液体,在浸锌后的镁合金AZ31表面实施恒流电镀铝,采用电化学技术评估镀铝层的耐蚀性,并采用SEM/EDX等技术表征镀层。结果表明：在浸锌后的镁合金表面可获得表面光洁的银白色镀铝层。在不同的电流密度下,呈现出两种形貌不同的镀铝层;在较佳电流密度12.3mA/cm2时,镀铝层表面较致密;电镀时间越长,镀层越厚,镀铝层耐蚀性越好。

简介：Fe(OH)3precursorsolwaspreparedbyasol-gelmethod.Theprecursorsolwasdippedontotheabsorbentcotton,andgelwasformedontheabsorbentcottontemplateafterthevolatilizationofmoisture.Fe2O3microtubulesweresynthesizedaftertheprocessofself-propagationorcalcination.Thephase,morphology,andparticlediameterofthesampleswereexaminedbyX-raydiffraction(XRD)andscanningelectronmicroscopy(SEM),andthemagneticpropertiesofthesamplesweremeasuredusingavibratingsamplemagnetometer(VSM).TheexternaldiametersofFe2O3microtubulesrangedbetween8and13μm,andthewallthicknessesrangedbetween0.5and2μm.ThetypeofthecalcinationmethodplaysasignificantroleindevelopingtheFe2O3phaseandthevariationinthemagneticpropertiesinthesol-geltemplatecomplexingmethod.γ-Fe2O3wassynthesizedbyaself-propagationmethod.However,α-Fe2O3wassynthesizedaftercalcinationat400°Cfor2h.Thecoercivityofthesamplessynthesizedbycalcinationat400°Cfor2hafterself-propagationwasfoundtoincreasesignificantly,therebypresentinghardmagneticproperties.

简介：Pt(Ⅱ)andPd(Ⅱ)complexeswith2',3',4',5,7-pentahydroxy-flavoneweresynthesizedandcharacterizedbyelementalanalysis,molarconductance,IR,1HNMR,TG-DTA,UV-Visspectroscopictechniques,andfluorescenceanalysis.Thescavengingeffectonthesuperoxideradical(O-2)andtheinhibitoryeffectonlipidperoxideswerealsoinvestigated.Boththeligandandthecomplexesexhibitscavengingeffectonsuperoxideradicals,andtheeffectofthecomplexesisgreaterthanthatoftheligand.ThePt(Ⅱ)complexexhibitsthestrongestscavengingefficiency.BothPt(Ⅱ)andPd(Ⅱ)complexeshavetheinhibitoryeffectonlipidperoxides,andtheeffectofthecomplexesisgreaterthanthatoftheligand,butthePt(Ⅱ)complexhasahigheffectofpromotinglipidperoxides.

简介：提出一种从黑泥中回收利用钛的新工艺,该工艺包括NaOH水热转化、水洗和H2SO4浸出制备TiO2。在优化的反应条件下,即NaOH溶液浓度为50%（质量分数）、NaOH/黑泥质量比为4：1、反应温度为240°C、反应时间为1h和氧气分压为0.25MPa,钛转化率可达97.2%,主要含钛产物是Na2TiO3。非目标产物Na2TiSiO5在水洗中保持稳定,在水热反应中提高NaOH浓度可以抑制Na2TiSiO5的生成。水热产物经过水洗后,97.6%的Na^＋可以回收。含有NaOH的溶液经过浓缩之后可以回用。在较低温度下,水洗物料中96.7%的钛能被较低浓度的硫酸浸出得到钛液。利用所得钛液进一步制备合格TiO2产品。

简介：采用计时电位、SEM、XRD、EIS和Tafel等方法对比研究Pb-Ag-Nd合金在160g/LH2SO4溶液中的脉冲电流极化和恒电流极化过程中的氧化膜和析氧行为。研究结果表明：脉冲电流极化的Pb-Ag-Nd合金表面的氧化膜孔洞更少,膜层更致密。这是由于在脉冲电流极化过程中的低电流阶段析氧反应更缓和,有利于多孔氧化膜的修复,因此低电流阶段可作为氧化膜的＂修复期＂。Pb-Ag-Nd阳极在脉冲电流极化过程中表现出更低的阳极电位,这与脉冲电流极化过程中阳极更小的传荷阻抗和高过电位区间更小的Tafel斜率相对应。更低的阳�

简介：ParkNelco公司的生产及工艺工程经理DougLeys先生撰文指出，当设计3～6GHz印制电路板时要注意考虑电路的趋肤效应、表面粗糙度、临近效应、电磁兼容性及介质基板材料等问题；并结合该公司的产品及有关技术数据，阐明了在选用高频电路基材时必须掌握的技术细节。同时本文中还搜集了一些低介电常数、低损耗因数基板材料的商品名称、型号及其主要技术数据。

简介：Mg–9Li–3Al–1.6Yalloyswerepreparedthroughmixturemethod.Themicrostructure,mechanicalproperties,andcorrosionresistanceoftheas-castandasextrudedalloyswerestudiedbyopticalmicroscopy（OM）,scanningelectronicmicroscopy（SEM）,X-raydiffraction（XRD）,mechanicalpropertiestesting,andelectrochemicalmeasurement.Theas-castMg–9Li–3Al–1.6Yalloywiththeaveragegrainsizeof325lmiscomposedofb-Limatrix,blocka-Mg,andgranuleAl2Yphases.Afterextrusion,thegrainsizeoftheas-castalloyisobviouslyrefinedandreachesto75lm;thestrengthandelongationoftheextrudedalloyareenhancedby17.20%and49.45%,respectively,owingtotheirfinemicrostructureandreductionofcastingdefects.Theas-extrudedalloyshowsbettercorrosionresistancecomparedtotheas-castone,whichmayberelatedtothelowstoredenergyanddislocationdensityintheextrudedalloy,alsothehomogenizationtreatmentbeforeextrusion.

简介：通过一个简单的水热方法成功地合成出由SnO2纳米片作次级结构的新型花状ZnSnO3-SnO2分级纳米结构。ZnSnO3多面体在生长分级SnO2纳米片的过程中主要起模版作用,制备出的SnO2纳米片的厚度约为25nm。还讨论了ZnSnO3-SnO2样品的形貌随反应时间变化的规律,并且进一步讨论了形成这种分级结构的形成机制。此外,由这种新型ZnSnO3-SnO2纳米结构作敏感材料的气体传感器对乙醇气体具有高灵敏和快响应的特点。ZnSnO3-SnO2纳米片在最佳工作温度270°C时,对50×10-6乙醇气体的灵敏度约为27.8,其响应和恢复时间分别在1s和1.8s内。