简介：AnO'-Sialon-Al2O3compositerefractorywaspreparedbyinsitureactionofSi3N4-ZrSiO4-Al2O3mixturewithfusedaluminaaggregates.Densification,insitureactionprocedureandmicrostructureofthematerialwereinvestigatedbymeansofX-raydiffraction,opticalandscanningelectronicmicroscopesandEDAX.

简介：MoltensaltsynthesisofMgAl2O4powderfromindustrialaluminaandlightcalcinedMgOinKCl,LiCl,andKCl-LiClmedia,andtheinfluenceofKFat500-1000℃wereinvestigated.SynthesizedpowderswerecharacterizedbymeansofXRD,laserparticleanalyzer,andSEM,andthesynthesismechanismofMgAl2O4wasdiscussedaswell.Theresultsshowthat(1)themoltensaltcomposite(KCl-LiCl)ismorefavorableforthesynthesisofMgAl2O4thansinglemoltensalt(LiClorKCl),andLiClismorefavorablethanKCl;(2)KFcanacceleratetheformationofMgAl2O4anddecreaseitsformingtemperature;(3)synthesisofMgAl2O4powderinthemoltensaltswithoutKFiscontrolledby'template-growth'mechanism,butinthemoltensaltswithKF,itiscontrolledby'template-growth'and'dissolution-precipitation'mechanism.

简介：Theroleofnano-SiO2andultra-fineboroncarbideonthepropertiesofalumina-graphitematerialswasinvestigated.Thestudyshowedthattheultra-fineboroncarbideaddedmodifiedthemicrostructureofresidualcarbonandpromotedthechemicalbondbetweenresidualcarbonfromphenolicresinandflakegraphite.Thecarbonwhitecouldstrengthentheresidualcarbonfromphenolicresin.ThesetwoadditivesimprovedthemechanicalpropertiesofAGrefractoriesatbothroomtemperatureandhightemperature,andthermalshockresistancewasimprovednoticeably.Whenthetwoadditivesweredopedtogether,carbonwhitecouldretardtheevaporationofB2O3.Thermalshockresistancewasguaranteedwithasmalleramountofultrafineboroncarbide.

简介：

简介：

简介：

简介：

简介：

简介：ThisworkstudiedthecharacteristicsofSiO2distributionandstructureofsilicatephasesinMgO-ZrO2compositessynthesizedbyrawmaterialsoflightfiredmagnesitendzircon,Theresultsindicatethat30wt%-40wt%SiO2contentinthesystemisexistedintheformofcrystallineofforsterite(M2S),theremainderingofSiOcontent(60wt%0-70wt%)isexistedintheglassphase,Thechemicalcompositionofglassphaseiswellagreedwiththechemicalcompositionofmonticellite(CMS).

简介：ThemagnesiabasedcurablespecimenswithdifferentSi3N4contentswerecastedusingsinteredmagnesite(w(MgO)=95%)asstartingmaterial,SiO2micro-powderasbinder,0.3%,4%and5%β-Si3N4powderreplacingtheequaladditionofmagnesiapowderrespectively.Theslagresistancetestwascarriedoutat1550℃for3husingBaosteeltundishslagandstaticcruciblemethod.Theresultindicatesthat:introducingSi3N4couldobviouslyimprovetheslagresistanceofMgObasedcastable,whichincreasedwithincreasingSi3N4.DenseSiO2sinteredlayerformedonthesurfaceofmagnesiabasedcastablebecauseoftheoxidationofSi3N4addition,whichcanpreventthefurtherslagpenetration.Inthedeepinnerofcastable,thepartial-pressureofoxygenwasverylow,soSi3N4canexiststably.Meanwhileinreducingatmosphere,Si3N4washardtobesintered,whichresultedinthelooseinteriorstructureofMgObasedcastable.

简介：Si3N4powderandhot-pressedSi3N4ceramicsaddedwithAl2O3areusedforinvestigatetheiroxidationbehviorinairandnitrogenatmosphere(withoxygenpartialpressurePO2=1-10Pa),TheoxidationproductsofSi3N4areexaminedbychemicalanalysi,X-raydiffraction(XRD)andXPSmethod,Also,thermodynamiccalculationismadetoanalyzeoxidationbehaviorofSi3N4.TheresultsshowthatonlypassiveoxidationwilloccurwhenSi3N4isoxidizedinairathightemperature,whereasinN2athightemperature,theactiveoxidationisdominantinspiteoftheexistenceofalittlepassiveoxidation.

简介：ThemechanicalpropertiesofpressurelesssinteringFe-Si3N4bondedSiCandSi3N4bondedSiCwithsamemanufactureprocesshavebeencomparedinthispaper.TheoxidizingmechanismofFe-Si3N4bondedSiCceramicmatrixcompositehasbeeninvestigatedespeciallythroughTG-DSC(thermogravimetricanalysis-differentialscanningcalorimeter)experiment.DuringoxidationprocedurethemainreactionistheoxidationofSiCandSi3N4,SiO2whichformprotectingfilmtopreventfurtheroxidizing.AndresidualironinthesamplesbecomeFe2O3andFe3O4,theoxidationkineticsat1100～1300℃ofre-Si3N4bondedSiChasbeenstudiedespecially.Theweightgainperunitareaatinitialstagechangesaccordingtobeelinerule,inthemiddleaccordingtoconic,andinthelastoxidationperiodfollowsparabolarule.

简介：

简介：β-sialon/alumina/silicamixturesweresinteredinflowingnitrogenat1500℃and1600℃respectively.ThesinteringpropertiesandmorphologyofsampleswereinvestigatedbySEM,EDSandXRD.Resultsshowthatsinteredpropertiesofthesamplesareinfluencedbysoakingtemperaturesandcompositions.Bulkdensitiesofsamplesareincreasedwiththeincreaseofthesoakingtemperature,whereastheapparentporositiesaredecreased.Masslossofthesinteredsamplesat1500℃islowerthanthatat1600℃,butallthemasslossremainsapproximatelyconstantwiththeincreaseofsialoncontent.Fromthepointofthermodynamicanalysis,ComplexchemicalreactionstakeplaceinsamplesduringsinteringprocessandthevolatileofSiO(g)isresponsibleforthemasslossofsamples.Comparedtocrosssectionmicrostructureofβ-sialon/Al2O3/SiO2mixturessinteredincokepowderbedconsistingofthedensecenterwithwell-developedcolumnofsialonphase,thetransitionalpartwithneedlelikegrainnitrogen-containingphaseandtheloosepartwithshortgranularAl2O3phase,thoseofmixturessinteredinflowingnitrogenisofwell-developedsialonindensecenterandslightlyloosepartwithsialondebris.

简介：MicrostructureandgrainboundarycharacterofhotpressedbinaryAl2O3(mullite,ZrO2)-SiCompositesandquaternaryAl2O3-mullite-ZrO2-SiCcompositewerestudiedbyelectronmicroscopyandmicroanalysis,ResultssuggestthatthereexistgrainboundarysolidsolutionsduetoelementaldiffusionnearSiCandmatrixoxidesgrainboundaries.

简介：LowcementAl2O3-SiO2castableswaspreparedusingsupergradebauxite(w(Al2O3)>85%)asaggregate,brownfusedcorundum,siliconcarbide,Secar71CAcement,α-Al2O3micropowderandmicrosilicaasfinepowders.TheinfluenceofSiC(0,5wt%,10wt%,and15wt%)onresistancetoPbO-richslagwasinvestigatedbystaticcrucibleslagtest(1300℃for5h,inair).TheslagcorrosionmechanismofthecastableswasanalyzedbymeansofSEM,EDSandXRD.TheresultsshowthattheresistanceofAl2O3-SiO2castablestoPbO-richslagisimprovedobviouslybytheadditionofSiC.ThecorrosionmechanismofthePbO-richslagcanbediscribedasthatPbOintheslagreactswithSiO2andCaOinAl2O3-SiO2castables,forminglow-meltingcompounds(suchasPbO·SiO2and2PbO·SiO2).

简介：MgO-Al2O3-Cr2O3rammingmixesmadeofdifferentrawmaterialshavedifferentmineralstructureanddifferentphysicalpropertiesthoughwiththeidenticalparticlesizedistribution,thesameamountofbinderandchemicalcomposition.Theresidualcarboncontentofthefusedmagnesia-chromematerialmadeinreducingatmosphereisveryhigh,ifthismaterialsisusedintheMgO-Al2O3-Cr2O3rammingmix,itwouldcausespallingofthefurnaceliningduringdrying-out.

简介：

简介：DenseSi3N4BNcompositeceramicswerefabricatedbysparkplasmasinteringat1500,1600and1650℃under50MPafor5minusingSi3N4andBNpowdersasstartingmaterialsand2mass%Al2O3and6mass%Y2O3assinteringadditives.ThevolumefractionofBNinSi3N4BNcompositepowderswaschosenas10%,20%,and30%,respectively.TheresultsofXRDandSEMshowthatα-Si3N4completelyturnsintoβ-Si3N4whenthecompositeceramicsaresinteredat1650℃;theadditionofBNhindersthegrowthofSi3N4grains,refiningthestructure;VickershardnessandfracturetoughnessofthecompositeceramicsdecreasewiththeincreaseofBNcontent.

简介：Inthispaper,theinflucnceofchiefprocessparametersontheontinuousproductionofSi3N4powderbyrenitridationhasbeenstudied,Thesutiableprocessparametershavebeenfound,andhighqualitySi3N4powderhasbeendeveloped.