简介：以超临界CO2为溶胀剂所制备的PET／PS共混物的小角X－射线散射（SAXS）研究表明，PET／PS共混物的结构参数与共混物的组成及热历史密切相关。按Vonk的一维电子密度相关函数法，得到共混物的结构参数。过度层厚随PS组分含量增加而增加，结晶片层厚却随PS含量增加而降低。热处理可提高共混物的结晶性。内比表面积随PS含量增加而增加是PS使PET韧性和抗冲击性能提高的本质原因。

简介：本文报道了作者在同步辐射X射线光刻研究中的一些新进展，其中，最细尺寸已达50纳米。

简介：StableoperatingregionintheHL-1Mtokamakhasbeenextendedbymeansofwallconditioning,corefuellingandcurrentcontroltechniques.Themechanismsoftheextensionareanalyzedinthispaper.Lithiumizationdiminishestheimpuritiesandhydrogenrecyclingtothelowestlevel.Afterlithiumizationahighdensityupto7×1019m-3wasobtainedeasilybystronggaspuffingwithordinaryohmicdischargealone.MoreattractivelywefoundthatmetalLi-coatingexhibitedtheeffectsofwallstabilization.Thelowqalimitwithhigherdensitywasextendedbyafactorof1.5～2incomparisonwiththatforboronization,and1.2forsiliconization.Siliconizationnotonlyextendedstableoperatingregionsignificantlybyitself,butalsoprovidedagoodtargetplasmaforotherexperimentsofraisingdensitylimit.Corefuellingschemesarefavourableespeciallyforsiliconizedwallwithahigherlevelofmedium-Zimpurity(Z=14).Aftersiliconizationthemaximumdensitynearto1020m-3wasachievedbyacombinationofsupersonicmoleculebeaminjectionandmultipelletinjection.ThenewdefinedslopeofHugilllimitillustratingmoreclearlythesituationunderlowqaandhighnedischargeswascreatedtoindicatethenewregionextendedbycombiningIpramp-upwithcorefuelling.TheslopewithalargeMurakamicoefficientincreasedbyafactorof50～60%.

简介：

简介：采用在位高压Raman光谱和高压同步辐射能散X射线衍射技术，在室温下对晶粒尺寸为10nm的锐钛矿TiO2进行了压致相变研究，压力范围分别为42．9GPa和23．0GPa，实验结果表明，在16．3GPaTiO2发生了一次结构相变，由原来的锐钛矿结构变为α－PbO2结构（TiO2-Ⅱ），该相变是不可逆的。同体材料TiO2的高压相变结果比较，由于晶粒尺寸的效应，纳米尺寸的锐钛矿TiO2的相变压力明显高于体材料的相变压力。

简介：

简介：Vacuumtreatmentandion-beambombardmentaretwomajorprocessesinthelowenergyion-beamimplantation.Toaccuratelystudythecontributionsofthesetwomajorfactorstothebioeffectsseparately,theM_1generationvariationofArabidopsisthalianawithion-beamimplantationandvacuumtreatmentwerecomparedthroughaseriesofkeyplantdevelopmentparametersincludingmorphologicalobservation,biochemicalassayandRAPD(randomamplifiedpolymorphicDNA)analysis.Theresultsshowedthation-beamimplantationhadobviouseffectonalmostalloftheseparameters,andthevacuumtreatmenthadsomeimpactsonseveralmorphologicalparameterssuchastheboltingtimeandthelengthoftheprimarystem.Takingtheresultstogether,theindicationisthatvacuumtreatmenthassomeslightcontributionstothebioeffectsofion-beamimplantationwhileion-beambombardmentitselfisthemajorcreatorofthebioeffects.

简介：利用北京同步辐射小角X光散射实验站，我们对超临界流体的抗溶剂过程中，高分子的构象变化进行了初步的研究。实验表明，在不断加入抗溶剂的过程中，高分子链发生了从伸展的无规线团到球形的转变。

简介：采用SRXRF对钧台窑汝瓷的元素谱进行了无损分析，研究了从釉经中间层到胎的元素分布特征。束斑为20×100μm的分祈数据表明钧台窑汝瓷中除了少数几个元素外、多数元素的分布是比较均匀的。用SRXRF无损分析汝瓷元素谱时，多数元素含量的结果可以得到重复，这为钧台窑汝瓷完整器物的分析鉴定提供了有应用价值的实验参数。

简介：同步辐射X射线（白光）微束激发晶态物质和非晶态物质时，其中晶态物质的衍射线将严重影响元素的X射线能谱分析，其最有效的解决办法是采用同步辐射单色光激发样品，或在样品与Si(Li)探测器之间入一准直器以消除衍射作用的影响。