简介：本文通过高分辨X射线衍射及掠入射(GID)的实验方法对生长在SrTiO3衬底上的LLa2/3Ca1/3MnO3和YBaCu3O7单层膜及YBa2Cu3O7-x/La2／3Ca1／3MnO3异质结构双层薄膜的微结构进行了研究。结果发现，所有薄膜都呈c向生长。由于热膨胀系数的不同而引起的热应力使得LCMO膜的晶格参数与靶材的相差较大。La2/3Ca1/3MnO3在单层腹及双层膜中都由靶材的立方结构变成了薄膜状态的四方结构。YBa2Cu3O7在单层膜及双层膜中都由靶材的正交结构变成了薄膜状态的四方结构。La2/3Ca1/3MnO3膜与YBa2Cu3O7膜在不同的样品中处于不同的应力状态。

简介：ThetransportpropertiesintheLa2/3(Ca1-xSrx)1/3MnO3(x=0,1/3,2/3)filmspreparedusingtheRFmagnetronsputteringmethodwereinvestigated.TheeffectoftheCa,Srdouble-dopingattheApositionintheLa2/3A1/3MnO3onthestructureofthetargetsandtransportofthefilmshasbeenstudied.Withtheincreaseofx,thestructuresofthetargetstransformfromtherhombohedralphasetothecubicphase;themetal-insulatorphasetransitiontemperature(Tp)ofthefilmsincreases;andthecorrespondingpeakresistivitydecreases.Allthephenomenacanbequalitativelyexplainedbythelatticeeffect.

简介：Duetotheremarkablemagnetoresistance(MR)effectonperovskite-typemanganite,magnetoelectronicsandspintronicshavebecomeattractivesubjectsofexperimentalandtheoreticalinvestigationsfortheapplicationpurpose.(La0.9Nd0.1)2/3Ca1/3Mn1-xFexO3(x=0,x=0.05)werepreparedsuccessfullybysol-gelmethod.Thestructure,magneticproperties,andtransportpropertiesofthecompoundswereinvestigated.Themagnetoresistanceeffectdependsonthecompositionandthetemperature.XRDpatternsshowthatthecompoundisasinglephasepolycrystalwithpseudocubicstructure.Alargenegativeisotropicmagnetoresistanceeffectinthesampleswereobservedatlowtemperatureregion.ThemaximumMRofthesampleswas77%and97%,respectively.Itwasmostlikelyduetothescatteringorthetunnelingtransportofspin-polarizedcarriersinlatticeunderstrongmagneticfield.

简介：美国宇航局在加州帕萨迪纳的喷气推进实验室研究成功了一种制造YBa2Cu3O7-α高温超导电缆（封装在金属套管内）的新方法。据称,这种方法成本较低,过程易于控制,且对各种前体材料有很强的适应能力。该法分4个步骤:生产具有化学（配）比的前体（Precursor）粉;将前体粉包封在金属套管内;用轧制的方法使前体粉固结;在液态锂金属浴槽内进行处理,使之转变成超导组

简介：ＳｃａｎｎｉｎｇＥｌｅｃｔｒｏｎＭｉｃｒｏｓｃｏｐｙＳｔｕｄｉｅｓｏｆＹＢａ＿２Ｃｕ＿３Ｏ＿（７－δ）ＳｕｐｅｒｃｏｎｄｕｃｔｏｒｓＳｈａＷｅｉ（沙维）（ＤｅｐａｒｔｍｅｎｔｏｆＣｉｖｉｌＥｎｇｉｎｅｅｒｉｎｇ，ＴｈｅＱｕｅｅｎ′ｓＵｎｉｖｅｒｓｉｔ...

简介：(1-x)La_(0.67)Ca_(0.33)MnO_3/Cr_2O_3(LCMO)+xCr_2O_3composites被一个新液相方法综合。XRD和SEM大小表明在LCMO结构和LCMO的晶格常数可溶的很少Cr_2O_3几乎没变化，当大多数Cr_2O_3在谷物边界或在LCMO谷物的表面上是分布式的时。Inresistivity对温度大小，金属--绝缘体转变被观察什么时候x<0.20。抵抗力增加和金属--绝缘体转变温度与Cr_2O_3的增加的内容减少。一个随机的电阻器网络(KRN)模型被使用，到模仿混合样品的运输性质。模拟结果同意试验性的观察。结果证明方法为理解maganite的composites的电子运输是合理的。

简介：用溶胶-凝胶法制备了系列掺杂（La0.8Ln0.2）2/3Ca1/3MnO3（Ln=La，Ce，Pr，Nd，Sm，Eu）纳米级晶体。对比在La被其它镧系元素部分替代后，引起的A位离子平均半径的改变和磁矩变化对电输运及磁阻性能的影响，实验分析表明，各个样品在同样大小磁场下的磁电阻存在较大的差别，样品的磁电阻随原子序数的增加而明显变大，由镧系收缩引起晶格畸变所产生的本征磁电阻占主导地位，随着外加磁场的增加，不同掺杂样品间的峰值电阻差异被弱化；各掺杂样品间的转变温度差与掺杂离子半径差和磁矩差密切相关，且离子半径的差异对转变温度的改变贡献更大。

简介：研究了ＹＢａＣｕ３Ｏ６～７超导催化剂上ＣＯ２的加氢制醇反应。考察了温度、压力和空速等条件对催化剂反应性能的影响。反应的主要产物是甲醇、ＣＯ和少量甲醚。利用ＸＰＳ、ＸＲＤ和ＡＦＭ等技术对催化剂的结构、铜的存在状态和反应活性位进行表征发现，在反应过程中，ＹＢａ２Ｃｕ３Ｏ６～７由ｏｒｔｈｏｍｂｉｃ相转变为ｔｅｔｒａｇｏｎａｌ相。反应活性位可能是Ｃｕ（Ｉ）物种。反应后催化剂颗粒的分散程度明显提高

简介：高质量的取向附生的YBa2Cu3O7-(YBCO)超导的电影被制作在上(OOl)用直流的劈啪作响方法的LaAlO3底层。不平常地高的电影厚度的成就(多达2.0嗯)没有microcracking，部分地被归因于毛孔的存在在这些电影与充满钇的作文相关。微观结构上的电影厚度的影响被X光检查衍射调查常规扫描(-2,-scan,杆数字)和印射的高分辨率的相互的空间。电影是没有直到2m的厚度的a-axis-oriented谷物面向的c轴。表面形态学和批评当前的密度(Jc)强烈取决于电影厚度。而且，为这些厚度依赖的原因详细被阐明。

简介：YBa2Cu3Ox(YBCO)thinfilmsgrownondifferentsubstrateswithand/orwithoutEu2CuO4(ECO)bufferlayerwereinvestigatedbyX-raywideanglediffraction,reflection,diffusescatteringandtopography.TheresultsshowthatfortheyttriastabilizedZrO2(YSZ)substrate,thepresenceofanECObufferlayerimprovesthecrystallinequalityoftheYBCOfilm,whileanegativeeffectisobservedfortheSrTiO3(STO)substrate.ThelateralcorrelationlengthforasamplegrownonaYSZsubstratewithECObufferLayerismuchgreaterthangrownonanSTOsubetrate.TheSTOsubstrateusedhasmosaicstructure.2001ElsevierScienceB.V.Allrightsreserved.

简介：Inordertorealizetheco-firingwithAg/Pdelectrodesinmultilayerdevices,Pb(Zn1/3Nb2/3)1-,-yZrxTiyO3(0.25＜x＜0.35,0.25＜y＜0.35)piezoelectricceramics(hereafterdesignatedPZN-PZT)modifiedbyLa2O3hasbeenpreparedbyconventionaltechniquewithsinteringtemperaturefrom1100℃to1140℃.X-raydiffractionpatternsdemonstratedthatpureperovskitephasewasobtained.Secondaryelectronimage(SEI)showedthatcrystallinegrainsinceramicswerewellgrown.d33ofmanufacturedsamplewasashighas560×10-12C/N.kpwasabout0.61andtgδabout30×10-3.TheexistenceofliquidphaseexaminedbyelectrondiffractioninPZN-PZTsampleisbeneficialtosinteringoftheceramic.

简介：Thenatureofresistivetransitionofhigh-qualitycrystallinethinfilmsofYBa2Cu3O7-δhasbeenstudiedundermagneticfields(H)appliedalongthecdirectionoverawiderangeofdopedholes,p,intheCuO2planes.Thefield-andtemperature-dependentin-planeresistivity,ρab(T,H),hasbeenanalyzedwithinthethermallyassistedflux-flow(TAFF)formalism.Thefluxactivationenergy,U(T,H),hasbeenextractedfromthisanalysis.Thelow-Tpartoftheρab(T,H)datacanbedescribedbyanactivationenergyhavingthefunctionalformofU(T,H)=(1-t)m(H-0/H)β,wheret=T/Tc(reducedtemperature),andH0isafieldscalethatprimarilydeterminesthemagnitudeofU(T,H).Thetemperatureexponent,m,showsasystematicvariationwithp,whereasthefieldexponent,β,isinsensitivetothepvaluesandisclosetounity.TheH0,ontheotherhand,changesrapidlyaspisvaried.U(T,H)islinkedtothepinningpotentialandconsequentlyonthesuperconductingcondensationenergy.Sincethenormalstatepseudogapdirectlyaffectssuperconductingcondensationenergy,aclearcorrespondencebetweenH0andthePGenergyscale,εg,isfound.Possibleimplicationsoftheseresultsarediscussed.

简介：

简介：Inthispaper,varioustechniquesincludingBET,XRD,SEMandXPSwereusedtostudythesinteringofpureandLa2O3-dopedtitania.Theexperimentalresultsshowthatsinteringoftitaniaproceedsviavolumediffu-sion.Addingoflanthanumoxidedecreasestherateofsinteringandhindersthephasetransitionfromanatasetorutilecrystalbystrongsurfaceinteractionbetweenthemixedcrystals(La4Ti9O24,La0.66TiO2.99)andTiO2.

简介：ThesplittingofpotentialenergylevelsforgroundstateX2ΠgofOx2(x=+1,1)underspin–orbitcoupling(SOC)hasbeencalculatedbyusingthespin–orbit(SO)multi-configurationquasi-degenerateperturbationtheory(SO-MCQDPT).TheirMurrell–Sorbie(M–S)potentialfunctionsaregained,andthenthespectroscopicconstantsforelectronicstates2Π1/2and2Π3/2arederivedfromtheM–Sfunction.TheverticalexcitationenergiesforOx2(x=+1,1)areν[O+12(2Π3/2→X2Π1/2)]=195.652cm1,andν[O12(2Π1/2→X2Π3/2)]=182.568cm1,respectively.Allthespectroscopicdataforelectronicstates2Π1/2and2Π3/2aregivenforthefirsttime.

简介：

简介：BondingofAl2O3tocuisperformeddirectlyusingTifoilattemperatureof1273K.Themicrostructureofthejointinterfaceisinuestigatedthroughscanningelectronmicroscope（SEM）,electron.probemicroanalysis（EPMA）andX-raydiffraction（XRD）.theeffectoftheinitialtifoilthicknessonthereactionlayerthicknessandthejointStrengthareinvestigated.

简介：VariousopticalluminescencespectroscopictechniqueswereusedtocharacterizethehighTcsuperconductorYBa2Cu3Ox.TheemissionbandsrevealthatCu3+coexistwithCu2+andCu+inthismaterial.

简介：设P为素数，利用同余及高次丢番图方程的一些结果证明了不定方程组x-1=3py^2，x^2＋x＋1=3z^2仅有正整数解（p，x，y，z）=（7，22，1，13）。

简介：本文主要研究添加微量稀土La2O3对Li2O-Al2O3-SiO2微晶玻璃晶相组成，显微结构，抗折强度的影响，研究结果表明：添加微量La2O3有利于Li2O-Al2O3-SiO2微晶玻璃中的主晶相β－锂辉石发育成完整的柱状，板状晶体，提高了微晶玻璃的抗折强度。