  • 简介:Fe3AlandCr18-Ni8steelwerebondedinvacuumandaninterfacewasformedbetweenFe3AlandCr18-Ni8steel.Stressdistributionatthediffusion-bondedinterfacewasresearchedbynumericalsimulationandfiniteelementmethod(FEM).TheresultsindicatedthatthepeakstressappearedattheinterfacenearCr18-Ni8steelside.Thisisthekeyfactortoinducecrackatthisposition.Withtheenhancementofheatingtemperature,thepeakstressatthebondedinterfaceincreases.Whenthetemperatureis1100℃,thepeakstressisupto65.9MPa,whichisbiggerthanthatat1000℃by9.4%.Inaddition,thepeakstressbecomesbiggerwiththeincreaseofthethicknessofbasemetalfrom1mmto8mm.Whilethethicknessismorethan8mm,thepeakstressvariesslightlywiththechangeofthethickness.

  • 标签: 压力分布 铁铝金属间化合物 扩散粘结 铬镍钢
  • 简介:焊接技术的发展都是以焊接高效率化和高产能化为最大目标。要实现高效率化焊接重要措施之一就是提高焊接速度,一般熔化极气保焊的焊接速度仅为0.3-0.5m/min。当焊接速度较高时(〉0.6m/min)易产生焊道不连续、咬边和产生大量气孔等缺陷,因而研究、推广焊接高效率化的技术成果是我国焊接领域里的重要课题。本文介绍一种在造船行业和钢结构焊接领域里常见型钢简捷、高效化平角焊接方法。即用双丝-熔池简捷高效快速焊接(焊接速度为1.2-1.5m/min,焊脚高度5mm)时也能达到良好的焊接规范和焊接性能的高效化平角焊接方法。经过多年的在造船行业和钢结构焊接中的T型钢焊接生产中证明,采用双丝-熔池气体保护焊可提高T型钢生产效率和焊接质量,减少焊接变形,因而双丝-熔池气体保护焊得到快速发展和广泛的应用。

  • 标签: 快速 高效率 简捷实用 易于推广
  • 简介:ESD(electrosparkdeposition)isapromisingprocesstoproducehardandwear-resistingcoatingsonmetallicsubstrates.InthispapermicrostructureandinterfacialcharacteristicsoftheWC92-Co8coatedontitaniumandcarbonsteelarepresented.Ametallurgicalbondingbetweenthecoatingandsubstrateisobtained.TheTielementwasfoundtodistributeinWC92-Co8atthemetalpool,aswellastheinterfacebydiffusion.SomenewphaseswereproducedinthecoatinglayerduetothechemicalreactionduringtheESDprocess.ExperimentalobservationandthermodynamicanalysiswereutilizedtostudythemechanismofESD.

  • 标签: WC92-Co8 硬质合金 电火花沉积 涂层 界面 ESD
  • 简介:Three-dimensionalfiniteelementmodelwasestablishedtosimulatetemperaturefieldsofT-jointtitaniumsheetsduringTIGweldingwithfiniteelementmethod(FEM)software.Temperaturedependentmaterialpropertiesandtheeffectoflatentheatwereconsidered.Atechniqueofelementbirthanddeathwasusedtosimulatetheprocessofweldedmetalfilling.DynamicvariationprocessoftemperaturefieldsduringTIGweldingwasachieved.Thesimulatedresultsagreedwellwiththemeasuredresults.

  • 标签: 钛合金 TIG焊接 温度场 有限元法 数字模拟
  • 简介:TiC/Cr18Ni8steelbondedcarbidesweresynthesizedbyvacuumsinteringwithmixedpowdersofiron,ferrotitanium,ferrochromium,colloidalgraphiteandnickelasrawmaterials.Themicrostructureandmicrohardnessofthesteelbondedcarbideswereanalyzedbyscanningelectronmicroscope(SEM),X-raydiffraction(XRD)andRockwellhardometer.ResultsshowthatthephasesofsteelbondedcarbidesmainlyconsistofTiCandFe-Cr-Nisolidsolution.ThesynthesizedTiCparticlesarefine.Mostofthemarenotmorethan1μm.Withtheincreaseofsinteringtemperature,theporosityofTiC/Cr18Ni8steelbondedcarbidesdecreasesandthedensityandhardnessincrease,butthesizeofTiCparticlesslightlyincreases.Underthesamesinteringconditions,thedensityandhardnessofsteelbondedcarbideswithC/Tiatomicratio0.9arehigherthanthosewithC/Tiatomicratio1.0.TheTiCparticleswithC/Tiatomicratio0.9aremuchfinerandmorehomogeneous.

  • 标签: 碳化钛 铬镍合金 不锈钢 钢结硬质合金 微观结构 反应合成
  • 简介:Inthisstudy,atwo-stepheatingprocessisintroducedfortransientliquidphase(TLP)diffusionbondingforsoundjointswithT91heatresistantsteels.Atfirst,ashort-timehighertemperatureheatingstepisaddressedtomelttheinterlayer,followedbythesecondsteptocompleteisothermalsolidificationatalowtemperature.Themostcriticalfeatureofournewmethodisproducinganon-planarinterfaceattheT91heatresistantsteelsjoint.WeproposeatransitionalliquidphasebondingofT91heatresistantsteelsbythisapproach.Sincejointmicrostructureshavebeenstudied,wetestedthetensilestrengthtoassessjointmechanicalproperty.Theresultindicatesthatthesolidifiedbondmaycontainaprimarysolid-solution,similarcompositiontotheparentmetalandfreefromprecipitates.Jointtensilestrengthofthejointisnotlowerthanparentmaterials.Jointbend'sstrengthsareenhancedduetothehighermetal-to-metaljunctionproducinganon-planarbondlines.Nevertheless,thetraditionaltransientliquidphasediffusionbondingproducesplanarones.Bondingparametersofnewprocessare1260℃for0.5minand1230℃for4min.

  • 标签: 液相扩散焊 T91钢 工艺 焊接接头 瞬时 等温凝固
  • 简介:Thefatiguepropertiesoffrictionstirwelded(FSW)buttjointandbasemetalofMB8magnesiumalloywereinvestigated.ThecomparativefatiguetestswerecarriedoutusingEHF-EM200K2-070-1AfatiguetestingmachineforbothFSWbuttjointandbasemetalspecimens.ThefatiguefractureswereobservedandanalyzedusingascanningelectronmicroscopeofJSM-6063LAtype.TheexperimentalresultsshowthatthefatigueperformanceoftheFSWbuttjointofMB8magnesiumalloyissharplydecreased.Theconditionalfatiguelimit(2×10~6)ofbasemetalandweldedbuttjointisabout77.44MPaand49.91MPa,respectively.Theconditionalfatiguelimit(2×10~6)oftheweldedbuttjointis64.45%ofthatofbasemetal.Themainreasonsarethattheweldingcanleadtostressconcentrationintheflasharea,tensileweldingresidualstressintheweldedjoint(Theresidualstressvaluewas30.5MPa),aswellasthegrainsizeisnotuniformintheheat-affectedzone.Thecleavagestepsorquasi-cleavagepatternspresentonthefatiguefracturesurface,thefracturetypeoftheFSWbuttjointbelongstoabrittlefracture.

  • 标签: 摩擦搅拌焊接 对接接头 摩擦焊接头 疲劳性能 基体金属 镁合金
  • 简介:Themicrostructureandmechanicalpropertiesoffrictionstirwelded2.5mm7050-77451aluminumalloynaturalaging72hand17520hwereinvestigated,respectively.Theuniaxialtensiletestshowedthatyieldstrength,tensilestrengthandelongationofthejoints17520hnaturalagingwereabout20%,12%and24%higherthanthosejointsnaturalaging72h.Hardnessprofileofnaturalaging17520hjointwitnessedsignificantenhancementinnuggetzone,comparedwith72hnaturalaging.Differentialscanningcalorimetry(DSC)andtransmissionelectronmicroscopy(TEM)testrevealedthatmoreGuinier-Prestonzone,η'andηphaseemergedinnuggetzoneasnaturalagingdurationincreased,highdensityofdislocationlocatedwithingrainboundaryinnuggetzoneofjointsnaturalaging72h.ItisconcludedthatnaturalagingwasfeasibletoenhancestrengthandplasticityofFSWjointssimultaneously.

  • 标签:
  • 简介:中国铁路总公司4月30日召开电话会议,再度调整今年的铁路固定资产投资计划,将今年铁路投资总额上调至8,000亿元人民币.仅次于2010年8426.52亿元的历史顶点。新项目从年初计划的44个飙升至64个,今年新投入运营的线路要确保达到7000公里以上,

  • 标签: 中国铁路 投资总额 设备 基建 电话会议 投资计划
  • 简介:Inthispaper,6mmthick2219-T6aluminumalloywasjoinedbymeansofvariablepolaritytungsten-arcwelding(VP-TIG)andtheinfluenceofgradientmismatchesonVP-TIGjointsisinvestigated.Theaveragetensilestrengthofthejointsreduces32%,53%and59%,whenthemismatchofthejointwas0.635mm,1.44mm,1.83mm,respectively.Incompletepenetration,additionalbendingmoment(Ma)anddecreaseofeffectiveloadregionareaareconsideredtoexplainthisphenomenon.Thefracturelocationoftensilespecimensoccurredattheweldzone(WZ)closetopartialmeltzone(PMZ),correspondingtoasharpdeclineofmicrohardnessfromPMZtoWZ.Theoriginalpositionoffractureisfoundatweldtoe,whereincompletepenetrationformsduetotheintroductionofgradientmismatches.

  • 标签: 2219-T6 aluminum alloy VP-TIG GRADIENT MISMATCHES
  • 简介:为了对高合金异种钢焊接工艺有更多的了解,本文通过对某火力电厂锅炉后屏过热器检修换管过程中涉及到的钢种(SA213-T91马氏体高合金耐热钢与Cr25Ni13奥氏体高合金耐热钢)的现场焊接工艺进行介绍,以给类似工程的施工提供一定的借鉴。

  • 标签: SA213-T91钢 Cr25Ni13钢 焊接工艺 异种钢焊接 活动夹块
  • 简介:Stationaryshoulderfrictionstirlapwelding(SSFSLW)wassuccessfullyusedtoweld6005A-T6aluminumalloyinthispaper.EffectofpinrotatingspeedoncrosssectionmorphologiesandlapshearstrengthoftheSSFSLWjointsweremainlydiscussed.Resultsshowthatjointswithoutflashandshouldermarkscanbeobtainedbythestationaryshoulder.CrosssectionoftheSSFSLWjointpresentsabasin-likemorphologyandlittlematerialloss.Byincreasingtherotatingspeedfrom1000rpmto1600rpm,botheffectivesheetthicknessandlapwidthincrease,whilelapshearfailureloadfirstlydecreasesandthenincreases.Themaximumfailureloadof14.05kNisattainedwhen1000rpmisused.AllSSFSLWjointspresentshearfracturemode.

  • 标签: 搅拌摩擦焊 铝合金焊接 旋转速度 剪切强度 搭接 抗剪强度