简介：通过单向拉伸试验研究镁合金AZ31B的电塑性效应。为了显示脉冲电流的非热效应,在相同温度下开展两类试验：环境箱中的单向拉伸试验和脉冲电流辅助的单向拉伸试验。此外,对脉冲电流在材料变形过程中引起的温度场进行数值模拟。结果表明,沿材料截面方向温度分布均匀。通过对比两类单向拉伸试验的真应力-真应变曲线,证实了脉冲电流非热效应的存在。通过光学显微镜研究脉冲电流对材料微观组织演化的影响,结果表明：脉冲电流引起的动态再结晶对流动应力的下降起重要作用。最后,提出一个考虑电塑性响应的AZ31B流动应力模型,并通过实验进行验证。结果表明：模型预测结果和实验结果吻合较好。

简介：RadiallyorientedNd–Fe–BringmagnetswerepreparedbybackwardextrusionofMQ-Cpowder.Thepunchchamferradiushasagreatimpactonthemicrostructureandmagneticpropertiesoftheringmagnet.Withthechamferradiuschangingfrom2,5to8mm,thecracksintheinnerwalldecreaseobviouslywhilethecrystallographicalignmentdrops.Furthermore,themechanismofcaxisgrowthwassuggestedtobeacombinationofsheardeformationinthecornerandsolution-precipitationunderthestressparalleltoradialdirection.Thealignmentdropsonthetopofringbecausethegrainsgrowfreelyandsometexturedgrainsgrowthroughnucleationandrecrystallization.Inthepresentwork,theoptimalpunchchamferradiusisfoundtobe2mm,andinthiscase,theremanence,coercivity,andmaximumenergyproductoftheringmagnetachieve1.4T,670kJám,and342kJám,respectively.

简介：疲劳性能是评估镁合金焊接结构寿命的重要指标。AZ31B镁合金TIG焊趾存在的微细裂纹与几何不连续,是在役焊接结构疲劳裂纹萌生的主要原因。为减轻接头的应力集中和改善其疲劳性能,采用CO2激光热源重熔AZ31B镁合金焊趾。研究发现：Mg17Al12在近熔合线的热影响区中沿晶界析出,而在焊缝中呈弥散分布。此外,因受脆晶相的作用,热影响区存在着微细裂纹。激光熔修能细化热影响区晶粒,抑制了Mg17A12沿晶界的析出从而有利于消除热影响区裂纹。然而因激光功率密度过高引起的镁元素烧损,是导致疲劳性能下降的一个重要原因。

简介：Thesegregationanddiffusionofboronduringheattreatmentswerestudied.Theinfluenceofboroncontents,agingtimeandappliedstressonFeMo2B2formationwasalsostudied.Finally,theeffectsofboroncontentsandFeMo2B2formationonthehightemperaturestrengthwerestudied.Boronatomsweresegregatedtoprioraustenitegrainboundaryduringnormalizingtreatment.Andtheseboronatomswereslowlydiffusedintothegraininteriorduringtemperingandagingat700℃.TheFeMo2B2phasewasonlyformedafter1,000hagingat700℃inalloycontaining196ppmboron.TheformationofFeMo2B2phaseisacceleratedbytheappliedstress.ItwasexpectedthattheformationofFeMo2B2iscloselyrelatedtotheredistributionofboronatoms.Thetensilestrengthsat700℃areincreasedwiththeincreaseofboroncontents.However,theformationofFeMo2B2phaseresultsinlowertensilestrength.

简介：B2Gold公司日前宣布完成尼加拉瓜ElLimon金矿扩建可研。目前E1Limon金矿整个矿区保有黄金资源储量达到1700万盎司，矿山中心区（Centralzone）保有黄金矿石量513万吨，中心区探明黄金储量81．2万盎司，探明矿石黄金平均品位4．92克/吨。

简介：针对AM60B合金在环境温度25～200℃、载荷12.5～300N的条件下进行干摩擦磨损实验。结果表明：随着载荷的增大,磨损率增加;从轻微磨损到严重磨损的转变的临界载荷分别为25℃时275N,100℃时150N,200℃时75N。在低载荷（〈50N）下,200℃下的磨损率低于25℃和100℃的。在轻微磨损阶段,磨损机制为磨粒磨损、氧化磨损和剥层磨损。当轻微磨损到严重磨损的转变开始时,剥层磨损发挥主要作用,剥层磨损是从基体内部发生的剥落。随后,塑性挤出磨损作为严重磨损出现,同时伴随着从轻微磨损到严重磨损的转变。厚的、硬的摩擦层通过限制磨面的塑性变形来阻碍从轻微磨损到严重磨损的转变。

简介：据来自中国有色金属工业协会的消息，初步统计分析显示，2007年规模以上有色金属工业企业实现主营业务收入或将达到17500亿元，是2002年的6．51倍：实现利润预计达到1300亿元，是2002年的16．15倍。

简介：1月8日讯据国土资源部网站报道，中国地质科学院地质力学所近日提交的“全国危机矿山接替资源找矿规划”项目——山东省招远市玲珑金矿田成矿规律和深部外围预测成果证实，该区深部发育第二富集带，矿田黄金资源总量超千吨。

简介：表里层有超细晶粒组织的SUF钢板是由新的热机调节技术法制造,超细晶粒表层部分的平均粒径不到2μm.因为SUF钢对脆性龟裂传播具有良好的阻止性能,所以它已成为伴有脆性破坏危险的船舶选用的钢板.

简介：TooptimizethemagneticpropertiesofnanocompositeNd9Fe85B6magnets,theas-quenchedribbonswithdifferentmicrostructureswerepreparedatsixwheelvelocitiesfrom10to30ms-1throughrapidquenching,followedbyaseriesofannealingtreatmentsat550–800°Cfor5–10min.Itisfoundthatboththelargeinitialgrainsatlowcoolingrateandhighcontentofamorphousphaseathighcoolingratecausea-Fegrainscoarsening,whichleadstoadeclineinthestrengthofexchangecouplinginteractionandthedeteriorationofmagneticproperties.Inordertooptimizethemagneticproperties,theas-quenchedribbonsshouldbechosenwithrelativelysmallinitialgrainsaswellasasmallamountofamorphousphase.FornanocompositeNd9Fe85B6materials,theoptimizedmagneticpropertiesofHcj=446kAm-1,Br=0.86T,(BH)max=80kJm-3areobtainedforribbonspreparedat18ms-1afterannealingat620°Cfor5min.

简介：GrainboundarydiffusiontechniquewithTbH_3nanoparticleswasappliedtofabricateTb-lesssinteredNdFe-Bpermanentmagnetswithhighcoercivity.Themagneticpropertiesandmicrostructureofmagnetsweresystematicallystudied.Thecoercivityandremanenceofgrainboundarydiffusionmagnetareimprovedby112%andreducedby26%comparedwiththoseoftheoriginalmagnet,respectively.Meanwhile,boththeremanencetemperaturecoefficient(α)andthecoercivitytemperaturecoefficient(β)ofthemagnetsareimprovedafterdiffusiontreatment.MicrostructureshowsthatTbelementenrichesinthesurfaceregionofNd_2Fe_(14)Bgrainsandisexpectedtoexistas(Nd,Tb)_2Fe_(14)Bphase.Thus,themagneto-crystallineanisotropyfieldofthemagnetimprovesremarkably.Asaresult,thesinteredNd-FeBmagnetsbygrainboundarydiffusionwithTbH_3nanoparticlesexhibitenhancedcoercivity.

简介：经过逾半年的停牌，银泰资源（000975）10月19日早间披露重大资产重组方案，拟12．03元／股发行3．74亿股，作价45亿元，收购埃尔拉多位于中国境内的金矿资产。

简介：铝基覆铜板是覆铜板体系中的一类重要产品，近年来全国已有十几家专业公司生产制造该产品，产能已达20万m^2左右。然而迄今尚无国家标准。制定该产品的国家标准，已是行业的迫切需要。

简介：采用放电等离子烧结(SPS)法将元素钛粉和镍粉制备成Ti-51%Ni形状记忆合金(SMAs)。研究目的是采用自由锻二次加工以提高SPS合金的性能。对自由锻前后合金的显微组织、相变温度和超弹性进行比较。结果表明，自由锻可以显著提高Ti-Ni形状记忆合金的拉伸强度和形状记忆性能，自由锻后合金的韧性从6.8%提高到了9.2%，超弹性的应变范围从5%增加到7.5%，应变恢复速率从72%提高到92%。Ti-51%Ni合金显微组织中含有立方奥氏体相(B2)基体、单斜马氏体相(B19′)、第二相(Ti3Ni4，Ti2Ni和TiNi3)和氧化物相(Ti4Ni2O，Ti3O5)。自由锻后再经500°C时效处理的最终样品的马氏体相变温度向高温方向偏移，这是由于Ti3Ni4相(透射电镜下可以观察到)的析出而导致基体中Ni含量的减少。总之，自由锻可以提高Ti-51%Ni形状记忆合金的超弹性和力学性能。

简介：为提高镁合金的耐蚀性,通过微弧氧化和硬脂酸乙醇溶液疏水处理两步法在镁合金表面制备超疏水涂层.考察微弧氧化电压、频率和时间对疏水处理试样接触角的影响.结果表明：随着微弧氧化电压、频率和时间的增加,疏水处理试样的接触角均先增大后减小,分别在350V、1000Hz和5min时获得最大值.最佳超疏水涂层主要由MgO和Mg2SiO4相组成,其表面微孔直径为～900nm,厚度为～6.86μm,接触角高达156.96°.超疏水试样的腐蚀电流密度较基体降低3个数量级,而氢气析出量较基体降低94.77%.

简介：超华科技（002288）2月20日晚间公告，根据《广东省著名商标认定和管理规定》和《广东省工商行政管理局关于广东省著名商标认定和管理的实施细则》的规定，经广东省著名商标评审委员会评审通过，公司“M”商标被延续认定为“广东省著名商标”，认定商品为“覆铜箔层压酚醛树脂板（绝缘材料）”，有效期自2013年3月24日起至2016年3月23日止。

简介：Al-3B中间合金是亚共晶Al-Si合金的高效细化剂之一。实验研究了Al-3B中间合金中未溶AlB2颗粒对Al-7Si合金晶粒细化的影响。结果表明,AlB2颗粒的数目和沉降对晶粒细化效果都有重要影响。在实验结果和理论分析基础上,提出了Al-3B中间合金对亚共晶Al-Si合金晶粒细化的新机制,认为通过共晶反应形成的＂Al-AlB2＂包覆结构是导致晶粒细化的直接原因,未溶的AlB2颗粒是α（Al）相的间接行核基底。

简介：种分氢氧化铝中碱含量变化规律关系到氢氧化铝的质量和碱耗，通过测定溶液浓度和电导率、氢氧化铝中碱含量和粒度分布以及分析粒子形貌，研究种分氢氧化铝中碱含量的变化规律。结果表明，溶液组分浓度高、球磨晶种循环、种分温度低、初始分解速率快或产品比表面积大都会导致氢氧化铝中碱含量升高；在低硅铝酸钠溶液种分过程中，粒子的附聚得到抑制，超细氢氧化铝中碱主要以晶格碱形式存在，以钠硅渣形式存在的碱含量极低；同时，升高初始分解温度，晶种老化，降低分解速率，延长种分时间，都有利于产品中碱含量的降低。结果还表明：种分过程中，Na＋Al（OH）4^-离子可能对产品中碱含量有很大的影响。

简介：进入2007年8月，国际白银价格走势紧随黄金，与其同步，不过当月银价的跌幅要比黄金要大。月初纽约贵金属走强，主要是美国公布的美国就业数据报告低于预期，引发美元的幅度下跌，直接刺激黄金价格达到一周来高点。3日纽约商品交易所（COMEX）白银主力合约9月期银（SIU7）价格较前日上涨0．163美元/盎司，定盘$13．158美元/盎司，交易区间为$12．985-$13．200．美元/盎司；当天纽约现货白银〈XAG〉价格定盘在$13．10／13．15美元/盎司，较前一交易日$12．94／12．99美元/盎司上涨。

简介：研究冷轧和后续退火形变热处理对Ni50Ti50形状记忆合金超弹性行为的影响。采用铜坩埚真空感应熔炼法制备样品。将成分均匀的样品进行热轧后在900°C退火，然后再进行冷轧，冷轧后样品的厚度有不同程度的减少，最大可达70%。透射电镜检测结果显示严重的冷轧导致Ni50Ti50合金中形成了纳米晶和非晶的复合显微组织。400°C下退火1h后，冷轧样品中的非晶发生晶化形成纳米晶组织。随着冷轧变形量的增加，在超弹性实验中Ni50Ti50合金的弹性应变增加，变形量为70%的冷轧-退火样品其弹性应变为12%。此外，随着变形量的增加，应力诱导马氏体相变的临界应力提高。值得注意的是，70%变形量的冷轧-退火样品的阻尼容量值为28J/cm3，明显高于商业NiTi合金。